Effect of Remineralization Products on the Microtensile Strength of Universal Dentin Bonding Systems.

Background/

Objectives

Adhesion to caries-affected dentin remains challenging due to its altered structure and composition. Remineralizing agents have been proposed to strengthen this substrate and improve bonding. This study evaluated the effect of three remineralization treatments, CPP-ACP, self-assembling peptide P11-4, and silver diamine fluoride (SDF), on the microtensile bond strength (μTBS) of universal adhesive systems applied to caries-affected dentin, using both etch-and-rinse and self-etch strategies.

Methods

Seventy human molars were sectioned and artificially demineralized to simulate caries-affected dentin. Samples were divided into ten groups: four untreated and six treated with CPP-ACP (MI Paste™), P11-4 (Curodont™ Protect), or SDF (Riva Star™). Universal adhesives were applied via etch-and-rinse or self-etch mode, followed by composite restoration. Microtensile bond strength was measured using a universal testing machine, and results were statistically analyzed with ANOVA and t-tests (p < 0.05).

Results

Untreated caries-affected dentin showed significantly lower μTBS than sound dentin (C3: 18.3 ± 5.4 MPa vs. C1: 41.3 ± 2.7 MPa). Remineralization agents improved μTBS considerably. CPP-ACP achieved the highest recovery (S1: 31.8 ± 2.6 MPa; S2: 29.2 ± 4.6 MPa), nearing sound dentin levels. P11-4 yielded moderate gains (S3: 24.4 ± 6.5 MPa; S4: 24.1 ± 4.7 MPa), while SDF provided the lowest, yet significant, improvements (S5: 23.7 ± 7.5 MPa; S6: 21.3 ± 5.3 MPa). Etch-and-rinse generally produced higher μTBS than self-etch, but differences were not statistically significant (p > 0.05).

Conclusions

Pre-treatment of caries-affected dentin with CPP-ACP, P11-4, or SDF enhances universal adhesive bond strength, with CPP-ACP showing the most pronounced effect. Remineralization protocols represent a valuable adjunct in restorative procedures involving compromised dentin.