The influence of acid etching time on the bonding performance of universal resin adhesives to dentin.
СтатьяНазвание и аннотация: Перевод пока не подготовлен
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Lu Chengyu, Pan Yahui, Nie Rongrong, Meng Xiangfeng
Аннотация
OBJECTIVE: To study the impact of different phosphoric acid etching time on the bonding strength and durability between two universal resin adhesives.
METHODS: The study was conducted at the Oral and Maxillofacial Surgery Department of the Affiliated Stomatological Hospital of Nanjing University Medical College, China, from August to October 2020, and comprised fresh human molars without caries that were exposed to the dentin surface. They were randomly divided into 4 groups based on different phosphoric acid etching time; 0s, 5s, 10s and 15s. Each group was bonded by composite resin columns with general resin adhesives Clearfil Universal Bond and All-bond Universal to form micro-tensile bonding specimens. After 24h of storage in distilled water, micro-tensile bond strength tests were carried out directly or after thermocycled for 10,000 cycles. After fracture, the bonding interface was observed by stereomicroscope and the fracture mode was recorded. Data was analysed using SPSS 22.
RESULTS: Of the 72 tooth specimens 18(25%) were in each of the 4 groups. Micro-tensile bond strength of Clearfil Universal Bond groups of 10s and 15s and All-bond Universal groups of 0s, 5s and 10s was higher than that of the other groups before and after thermocycling (p<0.05). The thermocycling treatment significantly reduced the micro-tensile bond strength of 0s, 10s and 15s groups of Al-bond Universal (p<0.01), but had no significant effect on Clearfil Universal Bond groups (p>0.05). The micro-tensile bond strength of 10s and 15s group of Clearfil Universal Bond was higher than that of corresponding groups of All-bond Universal groups before and after thermocycling (p<0.05).
CONCLUSIONS: Etching time of dentin surface could affect the micro-tensile bond strength and durability of universal resin adhesives.
METHODS: The study was conducted at the Oral and Maxillofacial Surgery Department of the Affiliated Stomatological Hospital of Nanjing University Medical College, China, from August to October 2020, and comprised fresh human molars without caries that were exposed to the dentin surface. They were randomly divided into 4 groups based on different phosphoric acid etching time; 0s, 5s, 10s and 15s. Each group was bonded by composite resin columns with general resin adhesives Clearfil Universal Bond and All-bond Universal to form micro-tensile bonding specimens. After 24h of storage in distilled water, micro-tensile bond strength tests were carried out directly or after thermocycled for 10,000 cycles. After fracture, the bonding interface was observed by stereomicroscope and the fracture mode was recorded. Data was analysed using SPSS 22.
RESULTS: Of the 72 tooth specimens 18(25%) were in each of the 4 groups. Micro-tensile bond strength of Clearfil Universal Bond groups of 10s and 15s and All-bond Universal groups of 0s, 5s and 10s was higher than that of the other groups before and after thermocycling (p<0.05). The thermocycling treatment significantly reduced the micro-tensile bond strength of 0s, 10s and 15s groups of Al-bond Universal (p<0.01), but had no significant effect on Clearfil Universal Bond groups (p>0.05). The micro-tensile bond strength of 10s and 15s group of Clearfil Universal Bond was higher than that of corresponding groups of All-bond Universal groups before and after thermocycling (p<0.05).
CONCLUSIONS: Etching time of dentin surface could affect the micro-tensile bond strength and durability of universal resin adhesives.