Fluoride Release, Recharge, and Mass Stability of Restorative Dental Materials: An In Vitro Study.

Background/

Objectives

Fluoride ion plays a crucial role in protecting teeth against caries by re-mineralizing the caries lesion. The objective of this study was to quantify and compare the fluoride release and recharge of restorative dental materials and their correlation with mass stability.

Methods

For this study, 5 × 5 × 2 mm blocks were prepared from GIC, RMGI L, GIOMER, Resin Composite, and RMGI R using a customized silicone index. The amount of fluoride released from each material was quantified using a fluoride electrode at 0 h, 1 day, 3 days, 1-week, and 2-week periods. The fluoride recharge of each material was calculated by quantifying the amount of fluoride uptake from high concentration fluoride solution over a period of 1-week. The mass stability of the materials was measured be quantifying the weight loss/weight gain during fluoride release and recharge phase. The correlation of fluoride release/recharge with weight loss/gain were analyzed using Pearson correlation.

Results

One-way ANOVA showed a statistically significant difference in the amount of fluoride released from each group (p < 0.05). The maximum amount of fluoride release was observed on the 3rd day in all the groups except the GIC group, which showed an ascending concentration of fluoride release till 2 weeks. One-way ANOVA showed statistically significant differences in weight loss/gain among the rested group (p < 0.05). GIC showed the highest amount of weight loss and weight gain among the tested materials.

Conclusions

The GIC material has the highest fluoride release and RMGI L has the highest fluoride recharge capability. The conventional GIC showed the least mass stability during fluoride release/recharge.