Effect of metal ions released from orthodontic mini-implants on osteoclastogenesis.

BACKGROUND

Orthodontic mini-implants can undergo corrosion and the release of metal ions can affect cellular behavior. Osteoclasts are involved in orthodontic tooth movement and implant stability. Osteoclasts and their precursors can be exposed to metal ions released from orthodontic mini-implants.

OBJECTIVES

This study aimed to investigate the effect of metal ions released from orthodontic miniimplants on human osteoclastogenesis.

MATERIAL AND

METHODS

Stainless steel and titanium alloy mini-implants were separately immersed in culture media for 14 days (days 1-14), and then moved to new media for a further 14 days (days 15-28). The concentration of the released metal ions was measured. Osteoclast precursors derived from human CD14+ monocytes were cultured in these media and in a control medium without mini-implant immersion. Cell viability, the number of osteoclasts and the area of resorption were investigated.

RESULTS

A higher concentration of metal ions was detected during the first 14 days as compared to the control. The concentration of these metal ions then declined after this period. The viability of osteoclast precursors was not affected by the released metal ions. There was a significant reduction in the number of osteoclasts when cultured in the medium with the titanium alloy mini-implants immersed for days 1-14. The area of resorption was also significantly reduced in this group. The media with the titanium alloy mini-implants immersed for days 15-28 and with the stainless steel mini-implants immersed for both study periods did not show statistically significant changes in the number of osteoclasts.

CONCLUSIONS

Metal ions were released from orthodontic mini-implants in the early period and declined thereafter. Metal ions released from titanium mini-implants in the early period inhibited osteoclastogenesis, while metal ions from stainless steel mini-implants had no effect on osteoclast differentiation.