Adverse effects of human pulps after direct pulp capping with the different components from a total-etch, three-step adhesive system.
СтатьяПоддержка исследования: вне правительства СШАНазвание и аннотация: Перевод пока не подготовлен
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Accorinte Maria de Lourdes Rodrigues, Loguercio Alessandro D, Reis Alessandra, Muench Antonio, de Araújo Vera Cavalcanti
Аннотация
OBJECTIVES: The objective was to evaluate the response of human pulps capped with different components from a total-etch three-step adhesive system.
METHODS: Direct pulp capping was performed in 25 caries-free human premolars scheduled for extraction due to orthodontic treatment. The teeth were randomly divided in five groups, and capped with the following materials: Group 1-acid+primer+adhesive were used as recommended; Group 2-only primer was applied; Group 3-only bonding resin (light-cured for 10s); Group 4-only composite resin (light-cured for 40s); Group 5-calcium hydroxide. After capping, all teeth were restored with ScotchBond Multi Purpose Plus and Z-100 was placed incrementally. After 60 days, the teeth were extracted and processed for light microscopic examination (H/E) according to a histological score system. These were subjected to non-parametric tests (alpha<0.05).
RESULTS: Overall, the histological features showed that groups 1-4 were quite similar and inferior to group 5. In groups 1-4 the pulp response varied from acute inflammatory cell infiltrate with varying degrees to necrosis. The groups 3 and 4 showed a trend towards better pulp response, since a normal connective tissue could be observed in more than half of the sample. All teeth from group 5 showed normal connective tissue below an amorphous dentin bridge.
SIGNIFICANCE: Adhesive components (primer or adhesive) as well as a composite should be avoided for pulp capping. Ca(OH)(2) should be the first choice for pulp capping.
METHODS: Direct pulp capping was performed in 25 caries-free human premolars scheduled for extraction due to orthodontic treatment. The teeth were randomly divided in five groups, and capped with the following materials: Group 1-acid+primer+adhesive were used as recommended; Group 2-only primer was applied; Group 3-only bonding resin (light-cured for 10s); Group 4-only composite resin (light-cured for 40s); Group 5-calcium hydroxide. After capping, all teeth were restored with ScotchBond Multi Purpose Plus and Z-100 was placed incrementally. After 60 days, the teeth were extracted and processed for light microscopic examination (H/E) according to a histological score system. These were subjected to non-parametric tests (alpha<0.05).
RESULTS: Overall, the histological features showed that groups 1-4 were quite similar and inferior to group 5. In groups 1-4 the pulp response varied from acute inflammatory cell infiltrate with varying degrees to necrosis. The groups 3 and 4 showed a trend towards better pulp response, since a normal connective tissue could be observed in more than half of the sample. All teeth from group 5 showed normal connective tissue below an amorphous dentin bridge.
SIGNIFICANCE: Adhesive components (primer or adhesive) as well as a composite should be avoided for pulp capping. Ca(OH)(2) should be the first choice for pulp capping.