Nanocomposites soft and hard denture liners containing ZrO2 nanoparticles: An in vitro evaluation of surface roughness and Candida albicans adhesion.
СтатьяНазвание и аннотация: Перевод пока не подготовлен
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Alshahrani Faris A, Albazroun Zainab, Alabdullatif Atheer, Aldehaileb Sarah, Khan Soban Q, Fouda Shaimaa M, Balhaddad Abdulrahman A, Abdelfattah Mohamed Y, Gad Mohammed M
Аннотация
PURPOSE: To investigate the impact of zirconium dioxide nanoparticles (nano-ZrO2) addition to hard and soft liners on the surface roughness and Candida albicans adhesion.
MATERIALS AND METHODS: Nano-ZrO2 was added to hard and soft chairside reline material in two concentrations (2% wt. and 4% wt.) while an unmodified group of each liner acted as a control, (n = 10). Disc-shaped (10 × 1.3 mm) specimens of hard denture reline (N = 60) and soft denture reline (N = 60) materials were prepared (30/test). A noncontact profilometer was used for surface roughness measurement. A colony-forming unit (CFU/mL) was used to evaluate Candida albicans adhesion. Data was analyzed using ANOVA and a post hoc Tukey's test (α = 0.05).
RESULTS: No significant change in surface roughness was observed with nano-ZrO2 addition; however, the control groups showed the highest value while 2% nano-ZrO2 showed the lowest value. In comparison to the control groups, nano-ZrO2 addition to the hard and soft liners significantly reduced Candida albicans adhesion (p < 0.001), regardless of the concentration.
CONCLUSION: Incorporating nano-ZrO2 into hard and soft liner had no effect on surface roughness while its addition reduced Candida albicans adhesion. Using chairside soft and hard liners containing nano-ZrO2 is recommended to reduce the incidence of denture stomatitis (DS) among denture wearers.
MATERIALS AND METHODS: Nano-ZrO2 was added to hard and soft chairside reline material in two concentrations (2% wt. and 4% wt.) while an unmodified group of each liner acted as a control, (n = 10). Disc-shaped (10 × 1.3 mm) specimens of hard denture reline (N = 60) and soft denture reline (N = 60) materials were prepared (30/test). A noncontact profilometer was used for surface roughness measurement. A colony-forming unit (CFU/mL) was used to evaluate Candida albicans adhesion. Data was analyzed using ANOVA and a post hoc Tukey's test (α = 0.05).
RESULTS: No significant change in surface roughness was observed with nano-ZrO2 addition; however, the control groups showed the highest value while 2% nano-ZrO2 showed the lowest value. In comparison to the control groups, nano-ZrO2 addition to the hard and soft liners significantly reduced Candida albicans adhesion (p < 0.001), regardless of the concentration.
CONCLUSION: Incorporating nano-ZrO2 into hard and soft liner had no effect on surface roughness while its addition reduced Candida albicans adhesion. Using chairside soft and hard liners containing nano-ZrO2 is recommended to reduce the incidence of denture stomatitis (DS) among denture wearers.