Journal of applied oral science : revista FOB · 2025
Comparison of TiF4, CPP-ACP, and NaF in preventing demineralization in irradiated bovine enamel and dentin in vitro.
СтатьяСравнительное исследованиеОценочное исследованиеНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Yao Lin, Li Yanyao, Fu Di, Ji Mengzhen, Zou Ling, Jiang Li
Аннотация
OBJECTIVES: To investigate the effects of sodium fluoride (NaF), casein phosphopeptide-amorphous calcium phosphate (CPP-ACP), and titanium tetrafluoride (TiF4) on the prevention of demineralization in irradiated bovine enamel and dentin in vitro.
METHODOLOGY: The enamel and dentin sample blocks were subjected to 50 Gy of radiation and divided into five groups (n=13): the deionized distilled water group, the NaF group, the CPP-ACP group, the NaF + CPP-ACP group, and the TiF4 group. After being treated with various materials for 30 minutes, the samples were remineralized for 12 hours and demineralized for 48 hours. The samples were then evaluated by scanning electron microscope (SEM), atomic force microscope (AFM), energy dispersive spectrometer (EDS), and transverse microradiography (TMR). Data were analyzed by ANOVA and the Kruskal-Wallis H test (α=0.05).
RESULTS: SEM and TMR indicated that the TiF4 group promoted more mineral deposits on the enamel and dentin samples, showing the least mineral loss and the lowest lesion depth. AFM results showed that the NaF + CPP-ACP group had the lowest enamel roughness (p<0.05), whereas the TiF4 group showed the lowest roughness in dentin samples (p<0.05). EDS showed that titanium (Ti) was deposited on the surface of the TiF4 group samples, whereas the NaF + CPP-ACP group more greatly aggregated fluorine.
CONCLUSION: TiF4 significantly impacted the prevention of demineralization in irradiated dental hard tissues. Combining NaF and CPP-ACP more effectively prevented demineralization than either agent used alone.
METHODOLOGY: The enamel and dentin sample blocks were subjected to 50 Gy of radiation and divided into five groups (n=13): the deionized distilled water group, the NaF group, the CPP-ACP group, the NaF + CPP-ACP group, and the TiF4 group. After being treated with various materials for 30 minutes, the samples were remineralized for 12 hours and demineralized for 48 hours. The samples were then evaluated by scanning electron microscope (SEM), atomic force microscope (AFM), energy dispersive spectrometer (EDS), and transverse microradiography (TMR). Data were analyzed by ANOVA and the Kruskal-Wallis H test (α=0.05).
RESULTS: SEM and TMR indicated that the TiF4 group promoted more mineral deposits on the enamel and dentin samples, showing the least mineral loss and the lowest lesion depth. AFM results showed that the NaF + CPP-ACP group had the lowest enamel roughness (p<0.05), whereas the TiF4 group showed the lowest roughness in dentin samples (p<0.05). EDS showed that titanium (Ti) was deposited on the surface of the TiF4 group samples, whereas the NaF + CPP-ACP group more greatly aggregated fluorine.
CONCLUSION: TiF4 significantly impacted the prevention of demineralization in irradiated dental hard tissues. Combining NaF and CPP-ACP more effectively prevented demineralization than either agent used alone.
Предметные рубрики MeSH
AnimalsCattleSodium FluorideCaseinsTitaniumDentinDental EnamelMicroscopy, Electron, ScanningTooth DemineralizationFluoridesTime FactorsCariostatic AgentsMicroscopy, Atomic ForceMaterials TestingMicroradiographySpectrometry, X-Ray EmissionReproducibility of ResultsAnalysis of VarianceStatistics, NonparametricSurface PropertiesReference ValuesTooth Remineralization