The Knee · 2021
Viscoelastic and failure properties of two configurations of triple-folded hamstring tendons used for anterior cruciate ligament (ACL) reconstruction.
СтатьяНазвание и аннотация: Перевод пока не подготовлен
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Orr Jeffrey, Sephien Andrew, Diaz Miguel A, Stoops T Kyle, Hamzavi Brian, Nofsinger Charles
Аннотация
BACKGROUND: Hamstring autografts are commonly used for anterior cruciate ligament (ACL) reconstruction. Different folding techniques exist in tripling the semitendinosus. Few anatomical studies exist in evaluating their viscoelastic properties. The purpose of this study was to characterize and compare the viscoelastic and failure properties of two hamstring graft configurations, the "Z" construct and "2" construct.
METHODS: Ten matched pairs of fresh-frozen cadaveric semitendinosus hamstring grafts were used to create the "2" configuration or "Z" configuration. The biomechanical testing consisted of four phases: preconditioning, where graft dimensions (mm) were measured; stress relaxation, where load, displacement and time data were collected and equilibrium relaxation (%) was calculated; dynamic creep, where the total construct elongation was calculated; and ramp-to-failure, where maximum failure load was recorded.
RESULTS: The "2" configuration demonstrated recorded forces (N) significantly greater at each time point when compared to the "Z" configuration during stress relaxation (p = 0.003). The "2" configuration exhibited significantly less construct elongation (mm) during dynamic creep at 10 cycles (p = 0.008) and 2000 cycles (p = 0.0001). The maximum measured load at failure was significantly greater in the "2" configuration constructs than "Z" configuration (p = 0.013). Moreover, the axial loads at 2, 3 and 4 mm of displacement were, on average, greater in the "2" configuration than "Z" configuration (p = 0.152; p = 0.080; p = 0.012), respectively.
CONCLUSION: The results of this study provide support for folding techniques for tripled grafts to provide higher viscoelastic and failure properties for techniques with less suture interfaces. Future studies can potentially evaluate the clinical significance of these findings.
METHODS: Ten matched pairs of fresh-frozen cadaveric semitendinosus hamstring grafts were used to create the "2" configuration or "Z" configuration. The biomechanical testing consisted of four phases: preconditioning, where graft dimensions (mm) were measured; stress relaxation, where load, displacement and time data were collected and equilibrium relaxation (%) was calculated; dynamic creep, where the total construct elongation was calculated; and ramp-to-failure, where maximum failure load was recorded.
RESULTS: The "2" configuration demonstrated recorded forces (N) significantly greater at each time point when compared to the "Z" configuration during stress relaxation (p = 0.003). The "2" configuration exhibited significantly less construct elongation (mm) during dynamic creep at 10 cycles (p = 0.008) and 2000 cycles (p = 0.0001). The maximum measured load at failure was significantly greater in the "2" configuration constructs than "Z" configuration (p = 0.013). Moreover, the axial loads at 2, 3 and 4 mm of displacement were, on average, greater in the "2" configuration than "Z" configuration (p = 0.152; p = 0.080; p = 0.012), respectively.
CONCLUSION: The results of this study provide support for folding techniques for tripled grafts to provide higher viscoelastic and failure properties for techniques with less suture interfaces. Future studies can potentially evaluate the clinical significance of these findings.