Effects of microabrasion and bleaching on color and shear bond strength of simulated stained-remineralized caries lesions.

PURPOSE: This study investigated the effects of bleaching and microabrasion on the color and shear bond strength (SBS) of stained-remineralized caries-like lesions (s-RCLs).

METHODS

Human enamel specimens were demineralized, stained (coffee/tea), then remineralized (2% NaF and artificial saliva [AS]) to create s-RCLs. Specimens were randomly divided into five groups (n = 18): G1, demineralized/AS; G2, s-RCLs/AS; G3, s-RCLs/at-home bleaching (15% carbamide peroxide [CP)], 6 h/d×7)/AS; G4, s-RCLs/microabrasion (6.6% hydrochloric acid, [1min/3cycles]/AS; and G5, s-RCLs/microabrasion and at-home bleaching/AS. Color was spectrophotometrically measured at baseline, after demineralization, after staining, and after treatment. After two weeks, the SBS was tested using a universal testing machine. Outcomes were analyzed using ANOVA models followed by Tukey's test (α = 0.05).

RESULTS

The mean colors (ΔE) for demineralization and staining were significant (ΔE ≤ 5.9 and ≤14.4, respectively). G3 (ΔE 23.9) and G5 (ΔE 25.2) were significantly improved compared to G4 (ΔE 12.3). The SBS in G5 had the highest significant value (25.2 MPa), followed by G4 and G3 (21.5-20.6 MPa), which were significantly higher than G2 (16.8 MPa). G2, in turn, was more significant than G1 (10.9 MPa).

CONCLUSION

At-home bleaching (15% CP) for seven days eliminated and improved organic stains on RCLs. Faster results were achieved when combined with microabrasion. All surface treatments resulted in high SBS.