Organo-Montmorillonite (OMMT) Modified SiC/Hydrogenated Epoxy Micro-Nanocomposites for Enhanced Corona Aging Resistance.

The concentration of electric fields at the end region of stator bars in large generators can readily induce corona discharge. Under long-term operation, corona discharge may cause drift in the surface conductivity and nonlinear coefficient of anti-corona materials, thereby weakening their capability to homogenize the tangential electric field. In severe cases, this can lead to charring failure of the anti-corona material. To improve the electrical-parameter stability and surface morphological resistance to corona aging of silicon carbide (SiC)-based anti-corona materials under long-term corona exposure, epoxy-resin-based anti-corona materials were investigated in this study. Scanning electron microscopy (SEM) and Fourier-transform infrared spectroscopy (FTIR) were first employed to analyze the effects of corona aging on the microstructure and chemical structure of the anti-corona layer, thereby revealing its failure mechanism. Subsequently, the evolution of surface conductivity, nonlinear coefficient, and surface morphology of bisphenol A epoxy resin (EP)- and hydrogenated bisphenol A epoxy resin (H-EP)-based anti-corona materials during 120 h of corona aging was comparatively investigated. On this basis, different mass fractions of organically modified montmorillonite (OMMT) were introduced into the H-EP-based anti-corona material for synergistic modification. The OMMT used in this study had a particle size of approximately 5 μm and an interlayer spacing of 2.6 nm, and its lamellar morphology and dispersion state in the epoxy matrix were characterized by cross-sectional SEM. Meanwhile, the trap-regulation mechanism of the OMMT-modified anti-corona materials was analyzed using isothermal surface potential decay (ISPD). The results show that erosion of the epoxy resin matrix by corona discharge is the primary cause of internal conductive-pathway disruption and anti-corona layer failure. Compared with the EP-based material, the H-EP-based material exhibited better conductivity and nonlinear stability during aging, although a certain degree of drift still occurred. The incorporation of an appropriate amount of OMMT further improved the corona resistance of the material. Among the investigated samples, the material containing 1 wt% OMMT showed the best performance, with its conductivity stabilized within the range of 10-13-10-11 S, the lowest variation rate of 104.76%, a relatively stable nonlinear coefficient, and slight surface damage. The ISPD results indicate that the interfaces introduced by OMMT increase the deep-trap density and suppress carrier migration, thereby stabilizing the conductive network. Overall, the synergistic effect of the H-EP matrix and 1 wt% OMMT can effectively enhance the corona resistance of SiC-based anti-corona materials.