Assessment of cytotoxicity, odontoblast-like differentiation, shear bond strength, and microhardness of four orthodontic adhesive composites.

PURPOSE: To determine and compare the cytotoxicity, odontoblast-like differentiation, shear bond strength (SBS) and Vickers microhardness of four commercial light-cured orthodontic adhesives.

METHODS

The orthodontic resins selected were Transbond XT - GI, Transbond Plus Color Change - GII (both from 3M Unitek), Enlight - GIII and Blugloo - GIV (both from Ormco). Samples were prepared, and leached monomers were obtained. Cytotoxicity was evaluated using the 3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide (MTT) assay and deposited calcium was analyzed using Alizarin red staining (ARS). SBS and the adhesive remnant index (ARI) were determined using 120 human premolars. The Vickers microhardness test was performed on the resin discs.

RESULTS

All adhesives showed moderate to severe cytotoxicity (21-37%) and promoted similar formation of calcium deposits. A SBS of 6-8 MPa was achieved only by Blugloo (7.1 ± 2.4 MPa), and Enlight showed the lowest Vickers hardness score (40 ± 2.5 HV). Transbond Plus Color Change (score 0 = 42.9%) and Blugloo (score 0 = 46.4%) showed better ARI scores than Transbond XT (score 0 = 7.1%) and Enlight (score 0 = 3.6%).

CONCLUSION

On the basis of the properties evaluated, Blugloo seems to be the best option.