An S-Infused/S, F-Codoped PVDF-Derived Carbon as a High-Performance Anode for Sodium-Ion Batteries.

Heteroatom doping is an effective strategy for improving the sodium storage performance of hard carbon. However, the use of sulfur and fluorine codoped carbon materials as anodes for sodium-ion batteries has not been reported. Here, an S-infused/S, F-codoped PVDF-derived carbon SFC5 was prepared by one-step carbonization of PVDF and synchronously used as an anode for a sodium-ion battery. The prepared SFC5 containing 10.11 at% S and 9.54 at% F is a short-range ordered amorphous carbon with a microporous structure. Owing to the structural advantages of S, F codoping, and the high specific capacity of S, SFC5 exhibited an outstanding sodium storage performance of 365 mAh g-1 after 200 cycles at 50 mA g-1 and 212 mAh g-1 after 500 cycles at 400 mA g-1. Moreover, theoretical calculations based on density functional theory (DFT) verify that S and F codoping can considerably reduce the Na+ adsorption energy and increase the electronic conductivity of SFC5. The current study presents a viable and facile approach to prepare high-performance, low-cost anode materials for SIBs, supported by empirical evidence and theoretical computations.