Biomimetic Remineralization of Artificial Caries Lesions with a Calcium Coacervate, Its Components and Self-Assembling Peptide P11-4 In Vitro.

The application of calcium coacervates (CCs) may hold promise for dental hard tissue remineralization. The aim of this study was to evaluate the effect of the infiltration of artificial enamel lesions with a CC and its single components including polyacrylic acid (PAA) compared to that of the self-assembling peptide P11-4 in a pH-cycling (pHC) model. Enamel specimens were prepared from bovine incisors, partly varnished, and stored in demineralizing solution (DS; pH 4.95; 17 d) to create two enamel lesions per sample. The specimens were randomly allocated to six groups (n = 15). While one lesion per specimen served as the no-treatment control (NTC), another lesion (treatment, T) was etched (H3PO4, 5 s), air-dried and subsequently infiltrated for 10 min with either a CC (10 mg/mL PAA, 50 mM CaCl2 (Ca) and 1 M K2HPO4 (PO4)) (groups CC and CC + DS) or its components PAA, Ca or PO4. As a commercial control, the self-assembling peptide P11-4 (CurodontTM Repair, Credentis, Switzerland) was tested. The specimens were cut perpendicularly to the lesions, with half serving as the baseline (BL) while the other half was exposed to either a demineralization solution for 20 d (pH 4.95; group CC + DS) or pHC for 28 d (pH 4.95, 3 h; pH 7, 21 h; all five of the other groups). The difference in integrated mineral loss between the lesions at BL and after the DS or pHC, respectively, was analyzed using transversal microradiography (ΔΔZ = ΔZpHC - ΔZbaseline). Compared to the NTC, the mineral gain in the T group was significantly higher in the CC + DS, CC and PAA (p < 0.05, Wilcoxon). In all of the other groups, no significant differences between treated and untreated lesions were detected (p > 0.05). Infiltration with the CC and PAA resulted in a consistent mineral gain throughout the lesion body. The CC as well as its component PAA alone promoted the remineralization of artificial caries lesions in the tested pHC model. Infiltration with PAA further resulted in mineral gain in deeper areas of the lesion body.