High-Resolution Characterization of Enamel Remineralization Using Time-of-Flight Secondary Ion Mass Spectrometry and Electron Microscopy.

INTRODUCTION

The aim of this in vitro study was to assess the suitability of high-resolution time-of-flight secondary ion mass spectrometry (ToF-SIMS) for visualizing cross-sectional changes in human enamel microstructure and chemical composition during treatment and remineralization cycling of artificially generated caries lesions underneath an artificial plaque.

METHODS

Treatments consisted of exposure to twice daily toothpaste/water slurries prepared from 0, 1,100, and 5,000 μg/g fluoride (F) NaF/silica toothpastes. In addition, treatments with slurries prepared from 1,100 μg/g F SnF2/silica toothpastes were done using 44Ca in the remineralization solution to allow for differentiation of newly formed mineral and exploration of incorporated metal dopants using ToF-SIMS. Complementary microhardness, scanning electron microscopy, and high-resolution transmission electron microscopy (HR-TEM) investigations were performed on enamel cross sections.

RESULTS

HR-TEM was used for the first time to determine the change in crystallinity during remineralization revealing distinct microstructural zones within one lesion. Chemical mapping using ToF-SIMS demonstrated that the distribution of F, while observed primarily in the new mineral phase, was widespread throughout the lesion with 44Ca substantially limited to the remineralizing mineral. Both penetrated the inter-rod spaces of the sound enamel illustrating how acid damage propagates into the native mineral as the caries lesion deepens. HR-TEM examination revealed different regions within the lesion characterized by distinct micro- and ultrastructures. Importantly, HR-TEM revealed a return of crystallinity following remineralization. F dose-response observations verified the ability of these high-resolution techniques to differentiate remineralization efficacy.

CONCLUSION

The collective results provided new insights such as the visualization of F or calcium penetration pathways, as well as new tools to study the caries process.