Protecting primary teeth from dental erosion through bioactive glass.

OBJECTIVES

The present study aimed to evaluate the effectiveness of bioactive glass (BAG) in preventing dental erosion in primary teeth.

METHODS

Enamel and dentin specimens (2 × 2 × 2 mm) were obtained from extracted primary teeth, which were randomly divided into the following groups based on the pretreatments (n = 12): DW (deionized water), NaF (2 % sodium fluoride), 2BAG (2 % BAG), 4BAG (4 % BAG), 6BAG (6 % BAG), and 8BAG (8 % BAG). The specimens were immersed in the respective solutions for 2 min and subjected to in vitro erosive challenges (4 × 5 min/d) for 5 d. The erosive enamel loss (EEL), erosive dentin loss (EDL), and the thickness of the demineralized organic matrix (DOM) were measured using a contact profilometer. The surface microhardness (SMH) was measured, and the percentage of SMH loss (%SMHL) was calculated. The surface morphology and mineral composition were evaluated by scanning electron microscopy (SEM) and energy-dispersive X-ray spectroscopy (EDS), respectively.

RESULTS

After the erosive challenges, the EEL, EDL, and%SMHL of the 2BAG, 4BAG, 6BAG, and 8BAG groups significantly reduced, with the greatest reduction was observed in the 6BAG (EEL: 6.5 ± 0.2 μm;%SMHL in enamel: 12.8 ± 2.6; EDL: 7.9 ± 0.3 μm; %SMHL in dentin: 22.1 ± 2.7) and 8BAG groups (EEL: 6.4 ± 0.4 μm;%SMHL in enamel: 11.0 ± 1.9; EDL: 7.8 ± 0.5 μm; %SMHL in dentin: 22.0 ± 2.5) (P < 0.05). With increasing BAG concentrations, the number of surface deposits containing Ca, P, and Si increased.

CONCLUSIONS

6BAG was the most effective for preventing dental erosion in primary teeth and showed a particularly strong potential for dentin erosion prevention.

CLINICAL SIGNIFICANCE: Bioactive glass, especially at a 6 % concentration, has proven effective in reducing erosive tooth wear and surface microhardness loss while also protecting demineralized organic matrix in primary dentin.