Effects of silver diamine fluoride on demineralization protection after a secondary acid challenge.
СтатьяНазвание и аннотация: Перевод пока не подготовлен
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Tudares Mauro A, Eckert George J, Lippert Frank
Аннотация
OBJECTIVE: This investigation describes the effects of 5% sodium fluoride varnish and 38% silver diamine fluoride on demineralization protection of human enamel lesions of three different severities after a secondary acid challenge.
STUDY DESIGN: Specimens underwent color and enamel surface microhardness change measurements after demineralization and treatment events. Transverse microradiography was conducted following the secondary demineralization.
RESULTS: After treatments, enamel surface microhardness change showed that 24-hour lesions treated with fluoride varnish had less rehardening than 24-hour lesions treated with silver diamine fluoride (p<0.05), whereas 144-hour lesions from both treatment groups showed a beneficial decrease in surface microhardness change that was markedly better in samples treated with silver diamine fluoride (p<0.05). After the secondary demineralization, 24- and 144-hour lesions treated with silver diamine fluoride showed a sustained beneficial decrease in enamel surface microhardness change when compared to fluoride varnish-treated samples of the corresponding lesion severity (p<0.05). Transverse microradiography showed no difference between fluoride varnish- and silver diamine fluoride-treated samples of any corresponding lesion severity, indicating that remineralization in both fluoride varnish- and silver diamine fluoride-treated samples was proportional to each other after a secondary acid challenge.
CONCLUSIONS: Using silver diamine fluoride may have comparable benefits to fluoride varnish in mineral loss prevention.
STUDY DESIGN: Specimens underwent color and enamel surface microhardness change measurements after demineralization and treatment events. Transverse microradiography was conducted following the secondary demineralization.
RESULTS: After treatments, enamel surface microhardness change showed that 24-hour lesions treated with fluoride varnish had less rehardening than 24-hour lesions treated with silver diamine fluoride (p<0.05), whereas 144-hour lesions from both treatment groups showed a beneficial decrease in surface microhardness change that was markedly better in samples treated with silver diamine fluoride (p<0.05). After the secondary demineralization, 24- and 144-hour lesions treated with silver diamine fluoride showed a sustained beneficial decrease in enamel surface microhardness change when compared to fluoride varnish-treated samples of the corresponding lesion severity (p<0.05). Transverse microradiography showed no difference between fluoride varnish- and silver diamine fluoride-treated samples of any corresponding lesion severity, indicating that remineralization in both fluoride varnish- and silver diamine fluoride-treated samples was proportional to each other after a secondary acid challenge.
CONCLUSIONS: Using silver diamine fluoride may have comparable benefits to fluoride varnish in mineral loss prevention.