Long-term bond strength of ormocer-based resin composites using a universal adhesive used in different adhesive strategies.
СтатьяРандомизированное исследованиеНазвание и аннотация: Перевод пока не подготовлен
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Cruz Marcelo Wa, Turssi Cecilia P, Amaral Flávia LBdo, Basting Roberta T, Viera-Junior Waldemir F, França Fabiana Mg
Аннотация
PURPOSE: To evaluate over time the bond strength to dentin of different resin composites (RBCs) associated with the universal adhesive system applied with self-etching or total-etching strategies.
METHODS: 60 human third molars were obtained, randomly divided into experimental groups (n= 10) according to RBCs: methacrylate-based nanofilled (Z350 XT); low-viscosity Ormocer-based bulk-fill (Admira Fusion X-base Universal); or high-viscosity Ormocer-based bulk-fill composite (Admira Fusion X-tra). The adhesion procedure was performed using a universal adhesive (Futurabond U) applied in self-etching or total-etching mode. Occlusal preparations (Class I) were made, measuring 4 mm in mesiodistal length, 4 mm in depth, and 3 mm in buccolingual height. The cavities were restored considering the RBCs and adhesive strategies, and the light curing was performed using a LED unit (BluePhase) as recommended by the manufacturers. For this, the nanofilled RBCs were inserted by the oblique incremental technique while the bulk-fill RBCs were inserted in single increments. The samples were stored in water for 24 hours in an oven; to be sectioned, the sticks were randomly separated, stored in distilled water for 24 hours (immediate) or 12 months (long-term), and taken to the universal machine for a microtensile test (MPa). The fractured sticks were examined to classify the type of fracture. The results were analyzed by ANOVA and Tukey's test (α= 0.05).
RESULTS: The MPa values of methacrylate-based nanofilled or high-viscosity Ormocer-based RBC were not affected by the strategy used to apply the universal adhesive system (P> 0.05). However, for the low-viscosity Ormocer-based RBC, higher values were obtained when the total-etching strategy was used compared to the self-etching mode (P< 0.05). After 12 months, when using the total-etching strategy low-viscosity Ormocer-based RBC, higher MPa values were obtained compared to the other materials (P< 0.05).
CLINICAL SIGNIFICANCE: Regardless of the adhesive strategy used, the high-viscosity RBCs, whether based on methacrylate or Ormocer, showed similar adhesive behavior. Low-viscosity Ormocer-based RBC showed greater long-term bond strength associated with the universal adhesive applied in the total-etching strategy.
METHODS: 60 human third molars were obtained, randomly divided into experimental groups (n= 10) according to RBCs: methacrylate-based nanofilled (Z350 XT); low-viscosity Ormocer-based bulk-fill (Admira Fusion X-base Universal); or high-viscosity Ormocer-based bulk-fill composite (Admira Fusion X-tra). The adhesion procedure was performed using a universal adhesive (Futurabond U) applied in self-etching or total-etching mode. Occlusal preparations (Class I) were made, measuring 4 mm in mesiodistal length, 4 mm in depth, and 3 mm in buccolingual height. The cavities were restored considering the RBCs and adhesive strategies, and the light curing was performed using a LED unit (BluePhase) as recommended by the manufacturers. For this, the nanofilled RBCs were inserted by the oblique incremental technique while the bulk-fill RBCs were inserted in single increments. The samples were stored in water for 24 hours in an oven; to be sectioned, the sticks were randomly separated, stored in distilled water for 24 hours (immediate) or 12 months (long-term), and taken to the universal machine for a microtensile test (MPa). The fractured sticks were examined to classify the type of fracture. The results were analyzed by ANOVA and Tukey's test (α= 0.05).
RESULTS: The MPa values of methacrylate-based nanofilled or high-viscosity Ormocer-based RBC were not affected by the strategy used to apply the universal adhesive system (P> 0.05). However, for the low-viscosity Ormocer-based RBC, higher values were obtained when the total-etching strategy was used compared to the self-etching mode (P< 0.05). After 12 months, when using the total-etching strategy low-viscosity Ormocer-based RBC, higher MPa values were obtained compared to the other materials (P< 0.05).
CLINICAL SIGNIFICANCE: Regardless of the adhesive strategy used, the high-viscosity RBCs, whether based on methacrylate or Ormocer, showed similar adhesive behavior. Low-viscosity Ormocer-based RBC showed greater long-term bond strength associated with the universal adhesive applied in the total-etching strategy.