Marginal Quality and Wear of Bulk-fill Materials for Class-II Restorations in Primary Molars.
СтатьяНазвание и аннотация: Перевод пока не подготовлен
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Hofmann Maria, Amend Stefanie, Lücker Susanne, Frankenberger Roland, Wöstmann Bernd, Krämer Norbert
Аннотация
PURPOSE: The aim of this in-vitro study was to evaluate the marginal integrity and wear of eight bulk-fill materials in comparison to a compomer in Class-II cavities in primary molars after thermomechanical loading (TML).
MATERIALS AND METHODS: Prepared Class-II cavities in 72 extracted primary molars were filled with eight bulk-fill materials. A compomer served as the control group. After water storage (incubator, 28 days, 37°C), samples were subjected to TML (2500 thermal cycles 5°C/55°C; 100,000 load cycles, 50 N, 1.67 Hz). Before and after TML, replicas were made which were used for both SEM analysis of marginal integrity and 3-D wear analysis. Statistical analysis was performed using Kruskal-Wallis and Wilcoxon tests (p < 0.05).
RESULTS: A significant reduction in perfect margins was observed for all groups, while marginal gap formation increased (Wilcoxon test, p < 0.02) for all groups but the compomer. Significant interindividual differences were observed between the tested materials regarding marginal integrity (Kruskal-Wallis test, p < 0.05). Wear analysis revealed no significant differences between groups (Kruskal-Wallis test, p > 0.05).
CONCLUSION: Some of the bulk-fill materials investigated here achieved better results than the compomer and should be further evaluated clinically.
MATERIALS AND METHODS: Prepared Class-II cavities in 72 extracted primary molars were filled with eight bulk-fill materials. A compomer served as the control group. After water storage (incubator, 28 days, 37°C), samples were subjected to TML (2500 thermal cycles 5°C/55°C; 100,000 load cycles, 50 N, 1.67 Hz). Before and after TML, replicas were made which were used for both SEM analysis of marginal integrity and 3-D wear analysis. Statistical analysis was performed using Kruskal-Wallis and Wilcoxon tests (p < 0.05).
RESULTS: A significant reduction in perfect margins was observed for all groups, while marginal gap formation increased (Wilcoxon test, p < 0.02) for all groups but the compomer. Significant interindividual differences were observed between the tested materials regarding marginal integrity (Kruskal-Wallis test, p < 0.05). Wear analysis revealed no significant differences between groups (Kruskal-Wallis test, p > 0.05).
CONCLUSION: Some of the bulk-fill materials investigated here achieved better results than the compomer and should be further evaluated clinically.