Dental materials : official publication of the Academy of Dental Materials · 2023
Evaluating the effect of preheating on resin composites in pit-and-fissure caries treatments with a digital intraoral scanner.
СтатьяПоддержка исследования: вне правительства СШАНазвание и аннотация: Перевод пока не подготовлен
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Yu Fan, Liu Bo, Lyu Changhai, Wang Xiaotong, Song Zijun, Ma Xueting, Fu Lilin, Rao Nanquan
Аннотация
OBJECTIVE: To evaluate the effect of preheating on the microleakage and surface hardness of resin composites in the treatment of pit-and-fissure caries with various widths, as measured by an intraoral scanner.
METHODS: A total of 153 L-shaped cavities with different widths (1 mm, 1.6 mm and 2 mm) were prepared on the buccal or palatal/lingual surfaces of human molars. The cavities were measured in three dimensions by a TRIOS scanner and then filled with various resins (room temperature Z350 flowable resin and room temperature and 60 ℃ Z350 universal resin). Microleakage and gap formation at 2 sites were evaluated by stereomicroscopy and scanning electron microscope. Resin samples were prepared, and the top surface Vickers hardness (VHNtop) of all samples was measured at 1 day and 30 days postirradiation.
RESULTS: No difference were observed in the 3D scans for the cavities sizes among groups with the same width. For the 1 mm-wide cavity, the lowest microleakage was obtained with the flowable group; for the 1.6 mm-wide cavity, the nonpreheating universal group showed the highest microleakage at site 1, and the preheating group exhibited lower microleakage than that of the nonpreheating universal group at site 2; and for the 2 mm-wide cavity, the preheating group presented lower microleakage at site 2. The gap formations were consistent with the microleakage degrees. The preheating group exhibited the highest VHNtop at 1 day and 30 days postirradiation.
SIGNIFICANCE: A digital intraoral scanner could be used to scan the cavities in three dimensions. Preheating technology could reduce the microleakage of Z350 universal resin and enhance its surface hardness.
METHODS: A total of 153 L-shaped cavities with different widths (1 mm, 1.6 mm and 2 mm) were prepared on the buccal or palatal/lingual surfaces of human molars. The cavities were measured in three dimensions by a TRIOS scanner and then filled with various resins (room temperature Z350 flowable resin and room temperature and 60 ℃ Z350 universal resin). Microleakage and gap formation at 2 sites were evaluated by stereomicroscopy and scanning electron microscope. Resin samples were prepared, and the top surface Vickers hardness (VHNtop) of all samples was measured at 1 day and 30 days postirradiation.
RESULTS: No difference were observed in the 3D scans for the cavities sizes among groups with the same width. For the 1 mm-wide cavity, the lowest microleakage was obtained with the flowable group; for the 1.6 mm-wide cavity, the nonpreheating universal group showed the highest microleakage at site 1, and the preheating group exhibited lower microleakage than that of the nonpreheating universal group at site 2; and for the 2 mm-wide cavity, the preheating group presented lower microleakage at site 2. The gap formations were consistent with the microleakage degrees. The preheating group exhibited the highest VHNtop at 1 day and 30 days postirradiation.
SIGNIFICANCE: A digital intraoral scanner could be used to scan the cavities in three dimensions. Preheating technology could reduce the microleakage of Z350 universal resin and enhance its surface hardness.