Implant dentistry · 2015
Bone regeneration of macropore octacalcium phosphate-coated deproteinized bovine bone materials in sinus augmentation: a prospective pilot study.
СтатьяНазвание и аннотация: Перевод пока не подготовлен
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Lee Jee-Ho, Kim Jin-Hong, Jeon Ju-Hong
Аннотация
OBJECTIVE: To investigate the osteogenic potential of macropore octacalcium phosphate (OCP)-coated deproteinized bovine bone materials (DBBMs) in sinus augmentation.
STUDY DESIGN: Macropore OCP-coated DBBM was manufactured from bovine bone by thermal and chemical processing. Sinus grafts of a lateral window approach with experimental bone were conducted in 10 patients. At 6 months after surgery, a total of 10 specimens were obtained from 10 patients. But, 4 of them were excluded because the amount of specimens was not enough for evaluation. Morphological investigation under scanning electron microscopy and histological evaluation were performed.
RESULTS: OCP was evenly attached to the surface of the experimental graft and showed a relatively large pore size (300-400 μm) compared with Bio-Oss (100-200 μm). New bone comprised 23.49% (± 0.10), and residual graft material comprised 15.39% (± 0.06) in bone specimens.
CONCLUSION: A macropore-sized design and OCP coating could present a favorable environment for new bone formation in maxillary sinus grafts.
STUDY DESIGN: Macropore OCP-coated DBBM was manufactured from bovine bone by thermal and chemical processing. Sinus grafts of a lateral window approach with experimental bone were conducted in 10 patients. At 6 months after surgery, a total of 10 specimens were obtained from 10 patients. But, 4 of them were excluded because the amount of specimens was not enough for evaluation. Morphological investigation under scanning electron microscopy and histological evaluation were performed.
RESULTS: OCP was evenly attached to the surface of the experimental graft and showed a relatively large pore size (300-400 μm) compared with Bio-Oss (100-200 μm). New bone comprised 23.49% (± 0.10), and residual graft material comprised 15.39% (± 0.06) in bone specimens.
CONCLUSION: A macropore-sized design and OCP coating could present a favorable environment for new bone formation in maxillary sinus grafts.