Thermo-Mechanical Characterization of GFRP Molded Grating Composites Exposed to Elevated Temperatures.

This study comprehensively investigates the thermal and mechanical degradation behavior of molded glass-fiber-reinforced plastic (GFRP) grating composites subjected to temperatures ranging from 80 °C to 320 °C. Three types of industrially produced GFRP gratings-open-type (OG), thin closed-skin (CG), and thick closed-skin (TCG)-were evaluated using mechanical, microstructural, chemical, and crystallographic analyses. Three-point bending tests revealed that TCG-type specimens exhibited superior thermal resistance, experiencing only a 43.9% loss in strength at 320 °C, whereas OG-type specimens showed significant resin degradation, fiber-matrix decomposition, and microcrack formation at temperatures above 200 °C. Scanning Electron Microscopy (SEM) and Fourier Transform Infrared Spectroscopy (FTIR) analyses revealed significant resin degradation, fiber-matrix decomposition, and microcrack formation. Thermogravimetric analysis (TGA) and Differential Scanning Calorimetry (DSC) confirmed substantial mass loss and structural disintegration at temperatures above 200 °C. Dynamic Mechanical Analysis (DMA) results revealed that the glass transition temperature (Tg) occurred at approximately 115-120 °C. The second-order regression model developed to estimate flexural strength under increasing temperature provided high accuracy (R2 > 0.99) for all grating types. It should be noted that this investigation focuses on the short-term thermo-mechanical response under fundamental flexural loading to provide an accurate baseline for preliminary engineering design. The findings emphasize that the effect of temperature should be considered a critical parameter in the structural design of GFRP systems, especially in industrial environments with temperatures above 120 °C. Accordingly, tables for material selection and load-carrying capacity should be recalibrated to account for short-term temperature effects.