Single-crystal growth, structure and thermal transport properties of the metallic antiferromagnet Zintl-phase β-EuIn2As2.

Zintl-phase materials have attracted significant research interest owing to the interplay of magnetism and strong spin-orbit coupling, providing a prominent material platform for axion electrodynamics. Here, we report the single-crystal growth, structure, magnetic and electrical/thermal transport properties of the antiferromagnet layer Zintl-phase compound β-EuIn2As2. Importantly, the new layered structure of β-EuIn2As2, in rhombohedral (R3̄m) symmetry, contains triangular layers of Eu2+ ions. The in-plane resistivity ρ(H, T) measurements reveal metal behavior with an antiferromagnetic (AFM) transition (TN ∼ 23.5 K), which is consistent with the heat capacity Cp(H, T) and magnetic susceptibility χ(H, T) measurements. Negative MR was observed in the temperature range from 2 K to 20 K with a maximum MR ratio of 0.06. Unique 4f7J = S = 7/2 Eu2+ spins were supposed magnetically order along the c-axis. The Seebeck coefficient shows a maximum thermopower |Smax| of about 40 μV K-1. The kink around 23 K in the Seebeck coefficient originates from the effect of the antiferromagnetic phase on the electron band structure, while the pronounced thermal conductivity peak at around 10 K is attributed to the phonon-phonon Umklapp scattering. The results suggest that the Eu2+ spin arrangement plays an important role in the magnetic, electrical, and thermal transport properties in β-EuIn2As2, which might be helpful for future potential technical applications.