Early bone healing to implants with different surface characteristics. A pre-clinical in vivo study.

AIM: To examine early bone healing around implants with non-modified and modified surfaces.

MATERIAL &

METHODS

Four implants with 4 different surface characteristics were installed in one side of the mandible following tooth extraction in 6 dogs. Implants in group A had a non-modified, turned surface, while implants in group B had a surface modification consisting of TiO-blasting and sequential acid-etching in oxalic and hydrofluoric acid. The surface modification of implants in group C was confined to sequential acid-etching in oxalic and hydrofluoric acid and Group D implants had a surface modification of TiO-blasting and acid-etching in hydrofluoric acid. The implant installation procedures were repeated in the opposite side of the mandible 4 weeks later. Biopsies were obtained and prepared for histological analysis 2 weeks later.

RESULTS

B and C implants had a higher degree of bone-to-implant contact (BIC%) than A and D implants at 2 weeks of healing. At 6 weeks of healing, the BIC% was higher at B than at A, C and D implants, and higher at C implants than at A implants. The amount of newly formed bone in contact with the implant within the defect area at 2 weeks was higher at implants with modified surfaces (groups B, C and D) than at implants with a non-modified surface (group A). Corresponding results at 6 weeks were superior at B implants.

CONCLUSION

It is suggested that an implant surface modification with acid-etching in oxalic and hydrofluoric acid promotes early formation of bone-to-implant contact.