Role of Amorphous Chains in Nanoplastic Formation from Semicrystalline Polymers.

Semicrystalline polymers, e.g., polyethylene terephthalate (PET), release micro- (100 nm to 1 mm) and nanoplastics (up to 100 nm) [MNPL] when they are degraded under quiescent conditions. However, the exact molecular mechanisms leading to material fragmentation into MNPL are unknown. Here, we monitor the evolution of chain molecular weight and the MNPL production kinetics during hydrolysis of PET pellets. We find that only ≈0.6% of the amorphous phase ester bonds are hydrolyzed at the onset of MNPL release. Then, by combining a random scission model with measured amorphous spacings, we estimate that only ≈15% of the stress transmitters in the amorphous phase, namely, bridges and entangled loops, have failed by this point. Thus, spontaneous fragmentation of the semicrystalline nanostructure occurs despite significant intercrystalline connectivity. We resolve this apparent contradiction by proposing that fragmentation can only occur when progressive tie-chain scission causes the material to undergo the ductile/brittle transition. Mechanistically, we speculate that the internal stresses responsible for material fragmentation are caused by processing (i.e., residual stresses) and/or sample densification induced by chemi-crystallization. We discuss additional factors that may affect our analysis and thus require further investigation, such as skin-core effects, preferential degradation of stress transmitters and/or recrystallization processes.