Physicochemical and Antibacterial Properties of a Mussel-Inspired Chlorinated Monomer Modified Dental Resin Matrix.
СтатьяНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Zhang Canwen, Huang Jiayi, Huang Mengyu, Zhang Yu, Jiang Haoyu, Chen Manling, Liang Peining, Yiu Cynthia Kar Yung, Li Kang
Аннотация
INTRODUCTION AND AIMS: Cariogenic biofilms at the resin-dentin interface frequently trigger secondary caries. This study aimed to synthesize a mussel-inspired chlorinated dopamine methacrylamide (Cl-DMA) monomer and evaluate its impact on the physical, antimicrobial, and biological properties of an experimental dental resin.
METHODS: Cl-DMA was integrated into a Bis-GMA/TEGDMA/HEMA matrix at mass ratios of 0, 1, 3, and 5 wt%. The physicochemical properties of Cl-DMA-modified resin matrix were evaluated by contact angle, water sorption, water solubility, degree of conversion, flexural strength, and modulus of elasticity. The release of Cl-DMA monomer from the resin matrix was monitored for 14 days using HPLC. Antimicrobial efficacy against Streptococcus mutans was quantified through CFU counting, CCK-8 assays, inhibition zone tests, scanning electron microscopy observation of biofilms, and fluorescent staining of live/dead bacteria. The in vitro cytotoxicity of the resin extracts was evaluated using L929 mouse fibroblasts via CCK-8 assay and live/dead staining observation.
RESULTS: Incorporating 1 to 3 wt% Cl-DMA preserved adequate immediate polymerization and mechanical strength, though a significant decline in flexural strength and modulus was observed across all groups after 28-day water ageing. Release kinetics strictly followed Fickian diffusion. The modified resins achieved a >2.5-log10 reduction in biofilm viability primarily via contact-killing. The 5 wt% group showed impaired polymerization, mechanical properties, and significant cytotoxicity.
CONCLUSION: Adding 3 wt% Cl-DMA endows dental resin with robust contact-killing capabilities without compromising immediate physical properties or biosafety. However, 28-day water ageing caused a significant decline in mechanical properties across all groups, indicating that the current unfilled resin formulation requires further optimization for long-term clinical application.
CLINICAL RELEVANCE: This chlorinated biomimetic monomer shows promise as an antimicrobial component for dental resin formulations; however, further investigation in long-term and in vivo models is required to assess its clinical potential.
METHODS: Cl-DMA was integrated into a Bis-GMA/TEGDMA/HEMA matrix at mass ratios of 0, 1, 3, and 5 wt%. The physicochemical properties of Cl-DMA-modified resin matrix were evaluated by contact angle, water sorption, water solubility, degree of conversion, flexural strength, and modulus of elasticity. The release of Cl-DMA monomer from the resin matrix was monitored for 14 days using HPLC. Antimicrobial efficacy against Streptococcus mutans was quantified through CFU counting, CCK-8 assays, inhibition zone tests, scanning electron microscopy observation of biofilms, and fluorescent staining of live/dead bacteria. The in vitro cytotoxicity of the resin extracts was evaluated using L929 mouse fibroblasts via CCK-8 assay and live/dead staining observation.
RESULTS: Incorporating 1 to 3 wt% Cl-DMA preserved adequate immediate polymerization and mechanical strength, though a significant decline in flexural strength and modulus was observed across all groups after 28-day water ageing. Release kinetics strictly followed Fickian diffusion. The modified resins achieved a >2.5-log10 reduction in biofilm viability primarily via contact-killing. The 5 wt% group showed impaired polymerization, mechanical properties, and significant cytotoxicity.
CONCLUSION: Adding 3 wt% Cl-DMA endows dental resin with robust contact-killing capabilities without compromising immediate physical properties or biosafety. However, 28-day water ageing caused a significant decline in mechanical properties across all groups, indicating that the current unfilled resin formulation requires further optimization for long-term clinical application.
CLINICAL RELEVANCE: This chlorinated biomimetic monomer shows promise as an antimicrobial component for dental resin formulations; however, further investigation in long-term and in vivo models is required to assess its clinical potential.
Предметные рубрики MeSH
Streptococcus mutansAnimalsAnti-Bacterial AgentsBiofilmsMiceMaterials TestingMethacrylatesPolymethacrylic AcidsMicroscopy, Electron, ScanningBivalviaComposite ResinsMicrobial Sensitivity TestsPolyethylene GlycolsPolymerizationResins, SyntheticFlexural StrengthBisphenol A-Glycidyl MethacrylateIndolesAcrylamides