Impact of liner treatment on the translucency of CAD/CAM multi-colored lithium disilicate and multi-layered zirconia implant-supported crowns, and evaluation of fracture strength of ceramic crowns.

This study aimed to evaluate the optical properties of liner-treated CAD/CAM Multi-colored lithium disilicate (Amber Mill Direct; AMD) and multi-layered zirconia (Omega multi; OM) implant-supported crowns, as well as their effect on the fracture strength of Ti or Zr abutments to which they were applied. After sintering AMD and OM ceramic blocks, they were classified into three groups: untreated, liner-treated, and liner-treated with added color. Optical properties were evaluated by analyzing color differences using background materials to assess translucency and the masking ability of liner-treated ceramics. Subsequently, the fracture strength of implant-supported crowns applied to Ti or Zr abutments was measured, and statistical analysis was conducted using Weibull statistics. Untreated AMD exhibited the highest translucency. Liner treatment reduced translucency in both ceramics, while color-added liner treatment increased translucency. Liner-treated AMD showed greater color difference compared to OM, whereas color-added liner treatment reduced the color difference. Fracture strength was highest in Ti abutment-OM crowns (548.03 N) and lowest in Zr abutment-AMD crowns (283.58 N). Additionally, the Weibull coefficient was over twice as high in Ti abutment-AMD crowns (m = 17.500). Color liners can adjust the high translucency of lithium disilicate ceramics to block discoloration, providing natural tooth-like color and enabling the creation of esthetic restorations. Furthermore, lithium disilicate ceramic crowns applied to Ti abutments exhibited high Weibull coefficients and fracture strengths.