Adventitial Collagen Cross-Linking by Glutaraldehyde Reinforcing Human Saphenous Vein - Implication for Coronary Artery Bypass Grafting.
СтатьяНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Liu Changcheng, Chen Duanduan, Li Zhenfeng, Xu Huanming, Gu Chengxiong
Аннотация
INTRODUCTION: A weak venous wall is one of the major reasons contributing to vein graft failure after coronary artery bypass grafting (CABG). We investigated whether adventitial collagen cross-linking by glutaraldehyde reinforces venous wall, preserving the endothelium of veins during high-pressure distention.
METHODS: Human saphenous veins (SVs) were collected from 40 patients undergoing CABG, and adventitia cross-linking was performed with 0.3% glutaraldehyde for five minutes. The cross-linked SVs were accessed by biodegradation assay, immunofluorescent staining, and tensile test. Native SVs and cross-linked SVs from another 20 patients received the 200 mmHg pressure distention for two minutes. Pressure-induced injury of SVs were accessed by immunohistochemistry and electron microscopy.
RESULTS: Time to digestion was 97±13 minutes for native SVs and 720±0 minutes for cross-linked SVs (P<0.05). After adventitial cross-linking, the collagen I fibres of the vein remarkably presented with compact and nonporous arrangement. In the high-stretch region (stretch ratio 1.4-1.8), the Young's elastic modulus of stress-stretch ratio curve in cross-linked SVs was larger than that in native SVs (13.88 vs. 5.83, P<0.05). The cross-linked SVs had a lower extent of endothelial denudation without fibre fracture during high-pressure distension than native SVs. Comparing with the non-cross-linked SVs, the percentage of endothelial nitric oxide synthase staining length on the endothelium of cross-linked SVs was significantly preserved after high-pressure distension (85.2% vs. 64.7%, P<0.05).
CONCLUSION: Adventitial collagen cross-linking by glutaraldehyde reinforced venous wall by increasing stiffness and decreasing extensibility of SVs and mitigated the endothelial damage under high-pressure distension.
METHODS: Human saphenous veins (SVs) were collected from 40 patients undergoing CABG, and adventitia cross-linking was performed with 0.3% glutaraldehyde for five minutes. The cross-linked SVs were accessed by biodegradation assay, immunofluorescent staining, and tensile test. Native SVs and cross-linked SVs from another 20 patients received the 200 mmHg pressure distention for two minutes. Pressure-induced injury of SVs were accessed by immunohistochemistry and electron microscopy.
RESULTS: Time to digestion was 97±13 minutes for native SVs and 720±0 minutes for cross-linked SVs (P<0.05). After adventitial cross-linking, the collagen I fibres of the vein remarkably presented with compact and nonporous arrangement. In the high-stretch region (stretch ratio 1.4-1.8), the Young's elastic modulus of stress-stretch ratio curve in cross-linked SVs was larger than that in native SVs (13.88 vs. 5.83, P<0.05). The cross-linked SVs had a lower extent of endothelial denudation without fibre fracture during high-pressure distension than native SVs. Comparing with the non-cross-linked SVs, the percentage of endothelial nitric oxide synthase staining length on the endothelium of cross-linked SVs was significantly preserved after high-pressure distension (85.2% vs. 64.7%, P<0.05).
CONCLUSION: Adventitial collagen cross-linking by glutaraldehyde reinforced venous wall by increasing stiffness and decreasing extensibility of SVs and mitigated the endothelial damage under high-pressure distension.