Optimization by mixture design of chitosan/multi-phase calcium phosphate/BMP-2 biomimetic scaffolds for bone tissue engineering.

The modulation of cell behavior during culture is one of the most important aspects of bone tissue engineering because of the necessity for a complex mechanical and biochemical environment. This study aimed to improve the physicochemical properties of chitosan/multi-phase calcium phosphate (MCaP) scaffolds using an optimized mixture design experiment and evaluate the effect of biofunctionalization of the obtained scaffolds with the bone morphogenetic protein BMP-2 on stem cell behavior. The present study evaluated the compressive strength, elastic modulus, porosity, pore diameter, and degradation in simulated body fluids and integrated these responses using desirability. The properties of the scaffolds with the best desirability (18.4% of MCaP) were: compressive strength of 23 kPa, elastic modulus of 430 kPa, pore diameter of 163 μm, porosity of 92%, and degradation of 20% after 21 days. Proliferation and differentiation experiments were conducted using dental pulp stem cells after grafting BMP-2 onto scaffolds via the carbodiimide route. These experiments showed that MCaP promoted cell proliferation and increased alkaline phosphatase activity, whereas BMP-2 enhanced cell differentiation. This study demonstrates that optimizing the composition of a mixture of chitosan and MCaP improves the physicochemical and biological properties of scaffolds, indicating that this solution is viable for application in bone tissue engineering.