Effects of montmorillonite on the loading and release of Piper betle L. extract applied for wound dressing based on chitosan/polyvinyl alcohol.

In this study, we investigate the influence of montmorillonite (MMT) on the loading and release of Piper betle L. extract (PLE)-a medicinal herb containing active secondary metabolites with antibacterial, antioxidant, and anti-inflammatory effects. MMT (1 %, 3 %, 5 %) was blended into the chitosan/polyvinyl alcohol (CS/PVA) biocomposite film by the solution evaporation method, and then PLE was loaded onto this biocomposite using the immersion method. The tensile strength and the ability to absorb exudates of the CS/PVA film improved with the increase in MMT content. The MMT 3 % film was considered to have the best properties: good mechanical properties with a tensile strength of 27.44 ± 0.27 MPa and elongation at break of 14.57 ± 0.30 %, potential for wound dressing due to its ability to absorb wound exudate (swelling degree 61.70 ± 0.30 %) and a suitable water vapor transmission rate (1999 ± 47 g/m2·d). The presence of MMT (1 %, 3 %, 5 %) in the CS/PVA film led to an increase in the PLE loading efficiency of the films compared to the film without MMT, up to 1.65, 1.73, and 1.87 times, respectively. The MMT 3 % and 5 % films also exhibited a sustained PLE release effect for up to 24 h. MMT increased PLE bioavailability through bioactivity tests: antibacterial activity against both E. coli and S. aureus, antioxidant activity, effective healing of 2nd-degree burn wounds, and biocompatibility with the L929 fibroblasts cell line. The combination of physicochemical properties and biological activities proved that the MMT/PLE drug delivery system based on the CS/PVA biocomposite is promising for wound dressing.