The treatment of femoral neck fracture using VEGF-loaded nanographene coated internal fixation screws.

PURPOSE: Previous studies have proved that vascular endothelial growth factor (VEGF) has a dual role in the promotion of new bone formation and blood vessel repair during fracture healing. However, how to introduce VEGF to a fracture site safely and effectively is still a challenge. This study aimed to prepare a VEGF-loaded nanographene coated internal fixation screw and to evaluate its effects in the treatment of femoral neck fracture.

METHODS

Nanographene coated screws were prepared by direct liquid-phase exfoliation of the graphite method, and the surface characteristics were observed through scanning electron microscopy (SEM). VEGF was loaded on nanographene coatings through physical adsorption, and the VEGF controlled release was examined by ELISA. Then a canine femoral neck fracture model was built to examine both the angiogenic and osteogenic properties of the VEGF-loaded coated screws. X-ray, micro-CT-based microangiography, and histopathologic evaluation were used to assess the fracture healing progress.

RESULTS

The results demonstrated that nanographene could load VEGF effectively, and the accumulative release of VEGF clearly increased during the entire testing period (9 days) without burst release. In canine fracture models, the results of X-ray, microangiography, and histopathologic examination proved that the speed of fracture healing, new bone formation area, and revascularization of the fractured femoral heads in the VEGF-loaded coated screws groups were significantly higher than in the control groups.

CONCLUSION

Our study proved that VEGF-loaded nanographene coated screws were effective in the treatment of femoral neck fracture and prevention of avascular necrosis of femoral head.