SnO2 Films Deposited by Ultrasonic Spray Pyrolysis: Influence of Al Incorporation on the Properties.

Aluminum-doped tin oxide (SnO 2:Al) thin films were produced by an ultrasonic spray pyrolysis method. The effect of aluminum doping on structural, optical, and electrical properties of tin oxide thin films synthesized at 420 ∘C was investigated. Al doping induced a change in the morphology of tin oxide films and yielded films with smaller grain size. SnO 2 thin films undergo a structural reordering and have a texture transition from (301) to (101), and then to (002) preferred cristallographic orientation upon Al doping. The lattice parameters (a and c) decreases with Al doping, following in a first approximation Vegard's law. The optical transmission does not change in the visible region with an average transmittance value of 72-81%. Conversely, in the near infrared (NIR) region, the plasmon frequency shifts towards the IR region upon increasing Al concentration in the grown films. Nominally undoped SnO 2 have a conductivity of ∼1120 S/cm, which is at least two orders of magnitude larger than what is reported in literature. This higher conductivity is attributed to the Cl- ions in the SnCl 4.5(H 2 O) precursor, which would act as donor dopants. The introduction of Al into the SnO 2 lattice showed a decrease of the electrical conductivity of SnO 2 due to compensating hole generation. These findings will be useful for further studied tackling the tailoring of the properties of highly demanded fluorine doped tin oxide (FTO) films.