Tailoring the Ni-O Microenvironment in Amorphous-Dominated Highly Active and Stable Zn/NiO for Hydrogen Sulfide Detection.

Amorphous metal oxide semiconductor (MOS) materials are endowed with great promise to modulate electronic structures for gas-sensing performance improvement. However, the elevated-temperature requirement of gas sensors severely impedes the application of amorphous materials due to their low thermal stability. Here, a cationic-assisted strategy to tailor the Ni-O microenvironment in an amorphous-dominated Zn/NiO heterogeneous structure with high thermal stability was developed. It was found that 6 mol % Zn incorporation into amorphous NiO can effectively preserve the amorphous-dominated NiO phase even at high temperature. After calcination, the amorphous oxide can only be converted to crystals partly thus leading to the formation of amorphous/crystalline compounds, and the content of the amorphous phase can be adjusted by changing the calcination temperature. This amorphous/crystalline configuration can induce more electron transfer from Ni to Zn species, leading to the formation of active Niδ+ (δ>2) centers. Ex situ XPS and in situ Raman spectroscopy studies proved that the generated Niδ+ species pronouncedly promote the electron transfer during the H2S adsorption process. The amorphous/crystalline-6 mol % Zn/NiO sensor exhibits exceptional hydrogen sulfide response (2 ppm, 3.23), outstanding repeatability (as long as 5 weeks), and low limit of detection (as low as 50 ppb), surpassing most reported nickel-based gas sensors such as the crystal nickel oxide prepared in this work. The response and detection limit of the latter is only (2 ppm, 1.89) and (0.05 ppm) respectively. Our work thus opens up more opportunities for fundamental understanding and modulating of highly active amorphous sensing materials.