Effects of lower alcohols on nanocomposite particles for inhalation prepared using O/W emulsion.
СтатьяНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Takeuchi Issei, Kimura Yukie, Nakajima Takehisa, Makino Kimiko
Аннотация
BACKGROUND: Inhalable nanocomposite particles using O/W emulsions were studied. The effect of the composition of the dispersed phase on the nanoparticles in the nanocomposite particles was reported, however, the effect on the inhalation characteristics of nanocomposite particles has not been investigated.
OBJECTIVE: The aim of this study was to study the effects of lower alcohols in the dispersed phase of O/W emulsions on inhalable nanocomposite particles.
METHODS: Nanocomposite particles were prepared using a spray dryer from O/W emulsion. A mixed solution of dichloromethane and lower alcohols in which rifampicin (RFP) and poly(L-lactide-co-glycolide) were dissolved was used as a dispersed phase, and an aqueous solution in which arginine and leucine were dissolved was used as a continuous phase.
RESULTS: We succeeded in preparing non-spherical nanocomposite particles with an average diameter of 9.01-10.91 μm. The results of the fine particle fraction (FPF) measurement showed that the higher the hydrophobicity of the lower alcohol mixed in the dispersed phase, the higher the FPF value. The FPF value of the nanocomposite particles was significantly increased by using ethanol and 1-propanol.
CONCLUSIONS: The results were revealed that mixing 1-propanol with the dispersed phase increased the amount of RFP delivered to the lungs.
OBJECTIVE: The aim of this study was to study the effects of lower alcohols in the dispersed phase of O/W emulsions on inhalable nanocomposite particles.
METHODS: Nanocomposite particles were prepared using a spray dryer from O/W emulsion. A mixed solution of dichloromethane and lower alcohols in which rifampicin (RFP) and poly(L-lactide-co-glycolide) were dissolved was used as a dispersed phase, and an aqueous solution in which arginine and leucine were dissolved was used as a continuous phase.
RESULTS: We succeeded in preparing non-spherical nanocomposite particles with an average diameter of 9.01-10.91 μm. The results of the fine particle fraction (FPF) measurement showed that the higher the hydrophobicity of the lower alcohol mixed in the dispersed phase, the higher the FPF value. The FPF value of the nanocomposite particles was significantly increased by using ethanol and 1-propanol.
CONCLUSIONS: The results were revealed that mixing 1-propanol with the dispersed phase increased the amount of RFP delivered to the lungs.