Effect of surface preparation on the bond strength of heat-polymerized denture base resin to commercially pure titanium and cobalt-chromium alloy.

The aim of this study was to investigate the bond durability of heat-polymerized denture base resin to cast CP Ti and Co-Cr alloy. The alloy specimens were divided into five groups: 1) airborne-particle abraded with 50 µm alumina (SAND), 2) Rocatec tribochemical silica coating system (RO), 3) air-abraded followed by application of Epricord Opaque Primer (EP), 4) air-abraded followed by application of Super Bond C&B liquid (SB), 5) air-abraded followed by application of Alloy Primer (AL). Heat-polymerized denture resin was applied to the bonding area and polymerized according to the manufacturer's instructions. The halves of all specimens were thermocycled up to 10,000 cycles. Before thermocycling SB and AL showed significantly higher shear bond strengths than SAND, RO, EP for both metals. The shear bond strength of AL group after thermocycling was significantly higher than that of the other groups.