Coeffect of pyrolysis temperature and potassium phosphate impregnation on characteristics, stability, and adsorption mechanism of phosphorus-enriched biochar.

Potassium phosphate (K3PO4)-impregnated bamboo was pyrolyzed at temperatures ranging from 350 to 950 °C to explore the coeffect of pyrolysis temperature and K3PO4 impregnation on biochar's characteristics and adsorption behavior. The degree of aromatization and graphitization in phosphorus-enriched biochars (PRBCs) rose as temperature increased, whereas H/C and O/C ratios, pH value, and O-containing group content decreased. The pre-aging impact of K3PO4 impregnation results in increased stability and adsorption performance of PRBCs. Adsorption mechanism of PRBCs to heavy metal varies from pyrolysis temperature. Micropores dominate medium-temperature PRBCs (prepared at 550 ∼ 750 °C), possessing the highest P-containing group content (116 % that of PRBC-350) and maximal adsorption capacity (greater than289 mg/g). The medium-temperature PRBCs adsorb Cd (II) via the role of O-containing groups, PO43-, and P2O74-, mainly by reactions of organic complexation, precipitation and inorganic complexation, respectively. 550 °C is the optimal pyrolysis temperature for both energy saving and heavy metal adsorption.