Journal of dentistry · 2024
Study on the polymerization shrinkage and mechanical-physical properties of dental resin composite modified by polyurethane dimechacrylate and glass flake fillers.
СтатьяПоддержка исследования: вне правительства СШАНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Feng Dan, He Xi, Dong Shunjun, Yang Zhengyuan, Zhang Lina, Zhu Song
Аннотация
OBJECTIVES: We intend to explore the polymerization shrinkage and mechanical-physical properties of the dental resin composite modified by polyurethane oligomer PU-MA and glass flakes fillers, and provide some experimental information for developing new dental materials.
METHODS: Based on Bis-GMA/TEGDMA, the new dental resin composite was hand fabricated by combining PU-MA with different content (65 wt% ∼ 75 wt%) of glass flakes/Si-Al-borosilicate glass mixed fillers. The kinetics of polymerization shrinkage was investigated by using an experimental set-up based on laser triangulation. The mechanical-physical properties of specimens after 60 days water immersion and 5000 times thermo-cycles were measured by three-point bending test and micro vickers hardness tester. Data were submitted to one-way ANOVA/LSD-test (α = 0.05). Independent sample T test was used to analyze the data before and after aging. Two-way ANOVA was adopted to analyze the effect of composition and aging condition on the mechanical-physical properties (α = 0.05).
RESULTS: PU-PG-75 % performs lower volume shrinkage (1.35%). As the increase of filler content, the water sorption and solubility increased and the depth of cure decreased significantly (P < 0.05). After aging, the flexural strength, elasticity modulus and vickers hardness of commercial products dropped obviously and PU-PG-75wt% was relatively stable.
CONCLUSIONS: 20 wt% PU-MA could decrease the volume shrinkage of dental resin composite effectively. 60 days water immersion and 5000 times thermal cycles simultaneously resulted in a significant reduction in the flexural properties for experimental materials. PU-PG-75 % may have the potential to be taken as a low shrinkage dental resin composite with good mechanical properties.
CLINICAL SIGNIFICANCE: This new synthesized composite could perform low polymerization shrinkage and better mechanical resistance, which may provide a new idea for improving the lifespan of direct restoration.
METHODS: Based on Bis-GMA/TEGDMA, the new dental resin composite was hand fabricated by combining PU-MA with different content (65 wt% ∼ 75 wt%) of glass flakes/Si-Al-borosilicate glass mixed fillers. The kinetics of polymerization shrinkage was investigated by using an experimental set-up based on laser triangulation. The mechanical-physical properties of specimens after 60 days water immersion and 5000 times thermo-cycles were measured by three-point bending test and micro vickers hardness tester. Data were submitted to one-way ANOVA/LSD-test (α = 0.05). Independent sample T test was used to analyze the data before and after aging. Two-way ANOVA was adopted to analyze the effect of composition and aging condition on the mechanical-physical properties (α = 0.05).
RESULTS: PU-PG-75 % performs lower volume shrinkage (1.35%). As the increase of filler content, the water sorption and solubility increased and the depth of cure decreased significantly (P < 0.05). After aging, the flexural strength, elasticity modulus and vickers hardness of commercial products dropped obviously and PU-PG-75wt% was relatively stable.
CONCLUSIONS: 20 wt% PU-MA could decrease the volume shrinkage of dental resin composite effectively. 60 days water immersion and 5000 times thermal cycles simultaneously resulted in a significant reduction in the flexural properties for experimental materials. PU-PG-75 % may have the potential to be taken as a low shrinkage dental resin composite with good mechanical properties.
CLINICAL SIGNIFICANCE: This new synthesized composite could perform low polymerization shrinkage and better mechanical resistance, which may provide a new idea for improving the lifespan of direct restoration.
Предметные рубрики MeSH
PolymerizationPolyurethanesComposite ResinsMaterials TestingHardnessPolymethacrylic AcidsDental MaterialsGlassMethacrylatesPliabilitySurface PropertiesPolyethylene GlycolsBisphenol A-Glycidyl MethacrylateWaterHumansAcrylic ResinsStress, MechanicalTime FactorsTemperatureElastic ModulusFlexural Strength