Bio-inspired fabrication of chitosan/PEO/Ti3C2Tx 2D MXene nanosheets supported palladium composite nanofiber catalysts via electrospinning.

In this study, novel chitosan/polyethylene oxide/Ti3C2Tx 2D MXene nanosheets (CS/PEO/Ti3C2Tx) nanofibers were successfully prepared by a continuous electrospinning process. During the electrospinning process, induced by the syringe tip capillary effects and electric field force, the Ti3C2Tx nanosheets were aligned along the direction of the nanofiber formation to occur a highly oriented structure. This well-ordered arrangement of the inorganic Ti3C2Tx nanosheets within the organic polymer matrix nanofiber was similar with nacre-like 'brick-and-motar' structure to some extent, resulting in a marked increase in thermal stability and mechanical properties of the resultant CS/PEO/Ti3C2Tx nanofiber. As 4 wt% of Ti3C2Tx nanosheets loaded, the highest tensile strength of the CS/PEO/Ti3C2Tx nanofiber mats was achieved as 31.7 MPa, about two times that of neat CS/PEO nanofibers. Uniformly dispersed Pd nanoparticles in size of about 1.6 nm have been successfully immobilized on the composite nanofiber with a solution impregnation process. With a loading as low as 0.2 mol% of Pd, the resultant Pd@CS/PEO/Ti3C2Tx composite nanofiber catalysts were highly active for both Heck and Sonogashira coupling reactions with broad reactants application scope, and could be recycled 15 runs without significant loss of activities.