Fluorescent cadmium telluride quantum dots embedded chitosan nanoparticles: a stable, biocompatible preparation for bio-imaging.

Fluorescent cadmium telluride quantum dots (CdTe QDs) are an optically attractive option for bioimaging, but are known to display high cytotoxicity. Nanoparticles synthesized from chitosan, a natural biopolymer of β 1-4 linked glucosamine, display good biocompatibility and cellular uptake. A facile, green synthetic strategy has been developed to embed green fluorescent cadmium telluride quantum dots (CdTe QDs) in biocompatible CNPs to obtain a safer preparation than 'as is' QDs. High-resolution transmission electron microscopy showed the crystal lattice corresponding to CdTe QDs embedded in CNPs while thermogravimetry confirmed their polymeric composition. Electrostatic interactions between thiol-capped QDs (4 nm, -57 mV) and CNPs (~300 nm, +38 mV) generated CdTe QDs-embedded CNPs that were stable up to three months. Further, viability of NIH3T3 mouse fibroblast cells in vitro increased in presence of QDs-embedded CNPs as compared to bare QDs. At the highest concentration (10 μg/ml), the former shows 34 and 39% increase in viability at 24 and 48 h, respectively, as compared to the latter. This shows that chitosan nanoparticles do not release the QDs up to 48 h and do not cause extended toxicity. Furthermore, hydrolytic enzymes such as lysozyme and chitinase did not degrade chitosan nanoparticles. Moreover, QDs-embedded CNPs show enhanced internalization in NIH3T3 cells as compared to bare QDs. This method offers ease of synthesis and handling of stable, luminescent, biocompatible CdTe QDs-embedded CNPs with a favorable toxicity profile and better cellular uptake with potential for bioimaging and targeted detection of cellular components.