Effect of build orientation on the manufacturing process and the properties of stereolithographic dental ceramics for crown frameworks.
СтатьяНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Dehurtevent Marion, Robberecht Lieven, Thuault Anthony, Deveaux Etienne, Leriche Anne, Petit Fabrice, Denis Corentin, Hornez Jean-Christophe, Béhin Pascal
Аннотация
STATEMENT OF PROBLEM: Stereolithography (SLA) ceramic crown frameworks are suitable for clinical use, but the impact of SLA build orientation has not been identified.
PURPOSE: The purpose of this in vitro study was to investigate the effect of 3 build orientations on the physical and mechanical properties and the microstructure of SLA alumina dental ceramics.
MATERIAL AND METHODS: The physical and mechanical properties and microstructures of 3 different oriented SLA alumina ceramics (ZX, ZY, and XY) were evaluated by visual observation, hydrostatic weighing (n=10/group), Weibull analyses (n=30/group), scanning electron microscopy, 3-point flexural strength (n=30/group), fracture toughness (indentation, single-edge-V-notched-beam) (n=4/group), and Vickers hardness (n=15/group) testing. The hydrostatic weighing, 3-point flexural strength, fracture toughness, and Vickers hardness testing data were statistically analyzed (α=.05).
RESULTS: The minimum resting period of slurries between the polymerization of 2 layers was shorter for the ZY- and ZX-oriented specimens and increased with the layer surface. The density and Vickers hardness of the SLA-manufactured specimens were similar for all groups (P>.05). The 95% confidence intervals of the Weibull moduli of the ZX- and ZY-oriented specimens were higher than that of the XY-oriented specimens, with no overlap fraction. The ZY-oriented specimens displayed significantly higher 3-point flexural strength (P<.05) and fracture toughness as evaluated by the single-edge-V-notched-beam method than the ZX-oriented specimens (P<.05). They also displayed significantly higher 3-point flexural strength than the XY-oriented specimens (P<.05). The microstructural analysis showed that the texturing was heterogeneous and that the major axis of the large grains of alumina ran parallel to the orientation of the layers.
CONCLUSIONS: The ZY orientation produced a reliable dental ceramic by SLA, with the shortest general manufacturing time and the highest mechanical strength when the layers were perpendicular to the test load surface.
PURPOSE: The purpose of this in vitro study was to investigate the effect of 3 build orientations on the physical and mechanical properties and the microstructure of SLA alumina dental ceramics.
MATERIAL AND METHODS: The physical and mechanical properties and microstructures of 3 different oriented SLA alumina ceramics (ZX, ZY, and XY) were evaluated by visual observation, hydrostatic weighing (n=10/group), Weibull analyses (n=30/group), scanning electron microscopy, 3-point flexural strength (n=30/group), fracture toughness (indentation, single-edge-V-notched-beam) (n=4/group), and Vickers hardness (n=15/group) testing. The hydrostatic weighing, 3-point flexural strength, fracture toughness, and Vickers hardness testing data were statistically analyzed (α=.05).
RESULTS: The minimum resting period of slurries between the polymerization of 2 layers was shorter for the ZY- and ZX-oriented specimens and increased with the layer surface. The density and Vickers hardness of the SLA-manufactured specimens were similar for all groups (P>.05). The 95% confidence intervals of the Weibull moduli of the ZX- and ZY-oriented specimens were higher than that of the XY-oriented specimens, with no overlap fraction. The ZY-oriented specimens displayed significantly higher 3-point flexural strength (P<.05) and fracture toughness as evaluated by the single-edge-V-notched-beam method than the ZX-oriented specimens (P<.05). They also displayed significantly higher 3-point flexural strength than the XY-oriented specimens (P<.05). The microstructural analysis showed that the texturing was heterogeneous and that the major axis of the large grains of alumina ran parallel to the orientation of the layers.
CONCLUSIONS: The ZY orientation produced a reliable dental ceramic by SLA, with the shortest general manufacturing time and the highest mechanical strength when the layers were perpendicular to the test load surface.