Characteristic Evaluation of Recombinant MiSp/Poly(lactic-co-glycolic) Acid (PLGA) Nanofiber Scaffolds as Potential Scaffolds for Bone Tissue Engineering.

Biomaterial-based nanofibrous scaffolds are the most effective alternative to bone transplantation therapy. Here, two recombinant minor ampullate spidroins (spider silk proteins), R1SR2 and NR1SR2C, were blended with Poly(lactic-co-glycolic) Acid (PLGA), respectively, to generate nanofiber scaffolds by electrospinning. The N-terminal (N), C-terminal (C), repeating (R1 and R2) and spacer (S) modules were all derived from the minor ampullate spidroins (MiSp). The physical properties and structures of the blended scaffolds were measured by scanning electron microscopy (SEM), water contact angle measurement, Fourier transform infrared spectroscopy (FTIR), Differential scanning calorimetry (DSC), and Tensile mechanical testing. The results showed that blending of MiSp (R1SR2 and NR1SR2C) reduced the diameter of nanofibers, increased the porosity and glass transition temperatures of nanofibrous scaffolds, and effectively improved the hydrophilicity and ultimate strain of scaffolds. It is worth noting that the above changes were more significant in the presence of the N- and C-termini of MiSp. In cell culture assays, human bone mesenchymal stem cells (HBMSCs) grown on NR1SR2C/PLGA (20/80) scaffolds displayed markedly enhanced proliferative and adhesive abilities compared with counterparts grown on pure PLGA scaffolds. Jointly, these findings indicated recombinant MiSp/PLGA, particularly NR1SR2C/PLGA (20/80) blend nanofibrous scaffolds, is promising for bone tissue engineering.