Supercritical antisolvent precipitation of PHBV microparticles.

The micronization of poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV) from organic solutions using supercritical antisolvent (SAS) technique has been successfully achieved. SAS experiments were carried out at different operational conditions and microspheres with mean diameters ranging from 3 to 9 microm were obtained. The effect of CO(2) and liquid flow, temperature and pressure on particle size and particle size distribution was evaluated. The microspheres were precipitated from a dichloromethane (DCM) solution. The best process conditions for this mixture were, according to our study, 40 degrees C, 100 bar, 1 mL min(-1) liquid flow and 10 L min(-1) carbon dioxide flow. Experiments with polymers containing different HV percentages were carried out. The powders obtained became more spherical as the HV content decreased.