Comparison of surface properties of universal shade and conventional resin-based composites after degradation and repolishing.
СтатьяСравнительное исследованиеНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Maesako Mayumi, Matsui Nagisa, Fujitani Morioki, Garcia-Godoy Franklin, Tsujimoto Akimasa
Аннотация
PURPOSE: To investigate the discoloration, line roughness and gloss of conventional and universal shade resin-based composites.
METHODS: Clearfil AP-X (AP-X) and Estelite Sigma Quick (EQ) samples were prepared. Discoloration, roughness, and gloss were measured on mirror-polished, alkaline-degraded, and repolished surfaces. The superficial layer degraded by alkaline immersion (degraded layer) was ground off from the sample surface. After removing the degraded layer, the surface was polished with aluminum oxide powder (1.0 µm and 0.3 µm), to create a repolished specimen. Scanning electron microscopy observations were made of the specimens.
RESULTS: The results were compared with those for Omnichroma (OC) from a previous study. All the materials showed different responses to degradation and repolishing, but repolishing of AP-X, for surface roughness and gloss, was more effective at restoring pre-degradation properties. Repolishing effectively removed discoloration in all materials.
CLINICAL SIGNIFICANCE: The materials tested showed different responses to degradation and repolishing, but repolishing of AP-X, for surface roughness and gloss, was more effective at restoring pre-degradation properties. Repolishing effectively removed discoloration in all materials.
METHODS: Clearfil AP-X (AP-X) and Estelite Sigma Quick (EQ) samples were prepared. Discoloration, roughness, and gloss were measured on mirror-polished, alkaline-degraded, and repolished surfaces. The superficial layer degraded by alkaline immersion (degraded layer) was ground off from the sample surface. After removing the degraded layer, the surface was polished with aluminum oxide powder (1.0 µm and 0.3 µm), to create a repolished specimen. Scanning electron microscopy observations were made of the specimens.
RESULTS: The results were compared with those for Omnichroma (OC) from a previous study. All the materials showed different responses to degradation and repolishing, but repolishing of AP-X, for surface roughness and gloss, was more effective at restoring pre-degradation properties. Repolishing effectively removed discoloration in all materials.
CLINICAL SIGNIFICANCE: The materials tested showed different responses to degradation and repolishing, but repolishing of AP-X, for surface roughness and gloss, was more effective at restoring pre-degradation properties. Repolishing effectively removed discoloration in all materials.