Synthesis, characterization and application of chitosan functionalized and functional graphene oxide membranes for desalination of water by pervaporation.

The use of graphene sheets in water treatment is increasing due to its adsorption capacity, reactivity, catalytic action and surface area. The challenges linked to wastewater treatment are vast due to the constant influx of various pollutants. Can the challenges of water desalination and purification be encountered by graphene-based composites and membranes?.The current work describes the synthesis of graphene oxide (GO) using modified Hummers' method. GO was functionalized with chitosan and used as adsorbents. On the other hand, it was reported that the surface of thin-film-composite (TFC) polyamide membranes was modified in order to desalinate highly saline water using pervaporation. The findings showed that GO synthesized by modified Hummers' method has a greater capacity for the adsorption of sodium ion and have better regeneration performance. Functionalization with chitosan increased adsorption capacity from 680.2 to 740.5 mg/g at the initial concentration of 45,000 mg/l of Na+ ions. On the other hand, modification in membrane comprises the chlorine treatment of surface of polyamide membrane. Layer-by-layer (LbL) deposition of positively charged polyethyleneimine (PEI) and negatively charged graphene oxide (GO) was followed. The PEI/GO LbL membrane's pure water flux was twice as high as compare to the original membrane. The synthesized membrane was tested against the aqueous solutions containing Na2SO4, MgSO4, NaCl and MgCl2 salts for their desalination. At different concentrations, a water flux of 8.9 kg/m2h with a huge salt rejection (>99.9%) was attained for every tested salt. It was observed that CS functionalized GO and GO membrane showed higher adsorption capacity and improved regeneration performance can be measured as an operational and active adsorbent for sea water desalination.