Corrosion casts of big bubbles formed during deep anterior lamellar keratoplasty.
СтатьяНазвание и аннотация: Перевод пока не подготовлен
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Feizi Sepehr, Kanavi Mozhgan Rezaei, Kharaghani Davood, Balagholi Sahar, Meskinfam Masoumeh, Javadi Mohammad Ali
Аннотация
PURPOSE: To characterize the walls of big bubbles formed during deep anterior lamellar keratoplasty (DALK) using the corrosion casting technique.
METHODS: Fresh corneoscleral buttons with normal transparency and without any known eye diseases (n = 11) were obtained from 11 human donors. A 20-gauge needle was used to inject a solution of 20 % polyvinyl alcohol (PVA) immediately beneath the corneal endothelium to form big bubbles in eight corneoscleral buttons. In the second experiment on three corneoscleral buttons, a big bubble was first formed by air injection beneath the endothelium. Thereafter, 20 % PVA was injected into the bubble space. Scanning electron microscopy was used to characterize the surfaces of the casts, which replicated the walls of the big bubbles.
RESULTS: A type-1 bubble was formed in all corneas. In one cornea, one type-1 bubble was initially formed centrally, and while it was enlarged, an eccentric type-2 bubble appeared. Scanning electron microscopy showed that the casts of type-1 bubbles had two distinct surfaces. The anterior surface demonstrated several holes or pits, depending on the material used for the bubble formation, whereas the posterior surface exhibited an uneven surface. The anterior and posterior surfaces of the type-2 cast were more or less similar. A communication measuring 531.9 µm in length and 171.4 µm in diameter was found between the two bubbles.
CONCLUSIONS: The corrosion casting technique provides a permanent three-dimensional record of the potential spaces and barriers in the posterior corneal stroma, which explains several features associated with big-bubble DALK.
METHODS: Fresh corneoscleral buttons with normal transparency and without any known eye diseases (n = 11) were obtained from 11 human donors. A 20-gauge needle was used to inject a solution of 20 % polyvinyl alcohol (PVA) immediately beneath the corneal endothelium to form big bubbles in eight corneoscleral buttons. In the second experiment on three corneoscleral buttons, a big bubble was first formed by air injection beneath the endothelium. Thereafter, 20 % PVA was injected into the bubble space. Scanning electron microscopy was used to characterize the surfaces of the casts, which replicated the walls of the big bubbles.
RESULTS: A type-1 bubble was formed in all corneas. In one cornea, one type-1 bubble was initially formed centrally, and while it was enlarged, an eccentric type-2 bubble appeared. Scanning electron microscopy showed that the casts of type-1 bubbles had two distinct surfaces. The anterior surface demonstrated several holes or pits, depending on the material used for the bubble formation, whereas the posterior surface exhibited an uneven surface. The anterior and posterior surfaces of the type-2 cast were more or less similar. A communication measuring 531.9 µm in length and 171.4 µm in diameter was found between the two bubbles.
CONCLUSIONS: The corrosion casting technique provides a permanent three-dimensional record of the potential spaces and barriers in the posterior corneal stroma, which explains several features associated with big-bubble DALK.