Micromorphological investigation of noncarious cervical lesions treated with demineralizing agents.
СтатьяПоддержка исследования: вне правительства СШАНазвание и аннотация: Перевод пока не подготовлен
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Sakoolnamarka R, Burrow M F, Prawer S, Tyas M J
Аннотация
PURPOSE: The purpose of this study was to examine the micromorphology of noncarious cervical lesions (NCCL) and the change occurring after acid conditioning.
MATERIALS AND METHODS: Nine wedge-shaped lesions, 9 saucer-shaped lesions, and 5 third molars with prepared cervical cavities were used. All NCCLs exhibited a hard, smooth surface with no discoloration. The teeth were sectioned and divided into three groups, each containing the three lesion types. Teeth in Group I were not etched, and teeth in Groups II and III were etched with 35% phosphoric acid and 20% polyacrylic acid/3% aluminum chloride, respectively. Field emission SEM and atomic force microscopy were used to examine the lesion surfaces.
RESULTS: The surfaces of the prepared cervical (control) lesions were covered with a smear layer. Treatment with phosphoric acid and polyacrylic acid resulted in removal of the smear layer, although some residual smear layer was found on the surface treated with polyacrylic acid. The images of the untreated surfaces of NCCL showed highly mineralized dentin with complete obliteration of the dentinal tubules. After treatment with phosphoric and polyacrylic acids, the images revealed demineralization of the surface, which was more pronounced on those treated with phosphoric acid.
CONCLUSION: The mineral deposits on the surface of NCCL decreased the effect of acid conditioning. Although there was no apparent difference between the two forms of NCCL used in this study, further work is needed to better understand these lesions.
MATERIALS AND METHODS: Nine wedge-shaped lesions, 9 saucer-shaped lesions, and 5 third molars with prepared cervical cavities were used. All NCCLs exhibited a hard, smooth surface with no discoloration. The teeth were sectioned and divided into three groups, each containing the three lesion types. Teeth in Group I were not etched, and teeth in Groups II and III were etched with 35% phosphoric acid and 20% polyacrylic acid/3% aluminum chloride, respectively. Field emission SEM and atomic force microscopy were used to examine the lesion surfaces.
RESULTS: The surfaces of the prepared cervical (control) lesions were covered with a smear layer. Treatment with phosphoric acid and polyacrylic acid resulted in removal of the smear layer, although some residual smear layer was found on the surface treated with polyacrylic acid. The images of the untreated surfaces of NCCL showed highly mineralized dentin with complete obliteration of the dentinal tubules. After treatment with phosphoric and polyacrylic acids, the images revealed demineralization of the surface, which was more pronounced on those treated with phosphoric acid.
CONCLUSION: The mineral deposits on the surface of NCCL decreased the effect of acid conditioning. Although there was no apparent difference between the two forms of NCCL used in this study, further work is needed to better understand these lesions.