Protein-mediated microbial biodegradation of high-density polyethylene: A comparative study of Bacillus cereus and Bacillus subtilis.
СтатьяСравнительное исследованиеНазвание и аннотация: Перевод пока не подготовлен
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Nawar Ali M, Mostafa Asmaa Mostafa, El-Kassas Seham, Rashwan Aya G, Abdelnasser Eman, Assas Mona
Аннотация
BACKGROUND: Plastic pollution, particularly microplastics, represents a persistent environmental threat due to their accumulation and ecological hazards. Biodegradation using bacteria provides a sustainable and ecofriendly strategy for mitigating plastic waste.
AIM: This study aimed to evaluate the biodegradation potential of B. cereus and B. subtilis against high-density polyethylene (HDPE) microplastics.
METHODS: A 9 × 9-cm HDPE film was inoculated with either bacterial strain in 100 ml Bushnell-Haas (BH) medium for 90 days. Biodegradation was assessed by povidone-iodine dye permeability, scanning electron microscopy, Fourier-transform infrared spectroscopy, weight loss measurement, light scattering, and sodium dodecyl sulfate (SDS)-polyacrylamide gel electrophoresis analysis.
RESULTS: The dye test revealed increased permeability, suggesting pore formation. Scanning electron microscopy confirmed structural modifications, with average pore diameters of 150.08 and 100.21 nm in Bacillus cereus and Bacillus subtilis, respectively. FT-IR indicated new functional groups and bond modifications, consistent with polymer chain breakdown. Weight loss analysis after 30 days showed reductions of 2.2% and 3.8% for B. cereus and B. subtilis, respectively. Light scattering demonstrated decreased plastic fragment size. SDS-polyacrylamide gel electrophoresis revealed the presence of extracellular proteins, including a ~100 kDa band in B. subtilis, implying enzymatic involvement in the degradation process.
CONCLUSION: Both B. cereus and B. subtilis degraded HDPE microplastics, with B. subtilis showing slightly higher efficiency. These findings support their potential as bioremediation agents for plastic-contaminated environments.
AIM: This study aimed to evaluate the biodegradation potential of B. cereus and B. subtilis against high-density polyethylene (HDPE) microplastics.
METHODS: A 9 × 9-cm HDPE film was inoculated with either bacterial strain in 100 ml Bushnell-Haas (BH) medium for 90 days. Biodegradation was assessed by povidone-iodine dye permeability, scanning electron microscopy, Fourier-transform infrared spectroscopy, weight loss measurement, light scattering, and sodium dodecyl sulfate (SDS)-polyacrylamide gel electrophoresis analysis.
RESULTS: The dye test revealed increased permeability, suggesting pore formation. Scanning electron microscopy confirmed structural modifications, with average pore diameters of 150.08 and 100.21 nm in Bacillus cereus and Bacillus subtilis, respectively. FT-IR indicated new functional groups and bond modifications, consistent with polymer chain breakdown. Weight loss analysis after 30 days showed reductions of 2.2% and 3.8% for B. cereus and B. subtilis, respectively. Light scattering demonstrated decreased plastic fragment size. SDS-polyacrylamide gel electrophoresis revealed the presence of extracellular proteins, including a ~100 kDa band in B. subtilis, implying enzymatic involvement in the degradation process.
CONCLUSION: Both B. cereus and B. subtilis degraded HDPE microplastics, with B. subtilis showing slightly higher efficiency. These findings support their potential as bioremediation agents for plastic-contaminated environments.