Dental adhesives incorporated with alkyl trimethyl ammonium bromide-loaded titanium oxide nanotubes for sustained bioactive and anti-biofilm protection.
СтатьяНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Garcia Isadora Martini, Araújo-Neto Vitaliano Gomes, Balbinot Gabriela, Souza Virgínia Serra, Mokeem Lamia, Scholten Jackson Damiani, Melo Mary Anne Sampaio, Giannini Marcelo, Collares Fabrício Mezzomo
Аннотация
OBJECTIVES: This study aimed to formulate experimental dental adhesives with alkyl trimethyl ammonium bromide-loaded titanium oxide nanotubes (ntTiO2/ATAB) and evaluated their physicochemical properties, antimicrobial activity, mineral deposition, and cytotoxicity.
METHODS: ntTiO₂/ATAB was synthesized, characterized, and added into an experimental adhesive resin. The filler ntTiO₂/ATAB was added at 1, 2.5, and 5 wt% (G1 %, G2.5 %, G5 %) in the adhesive. A control group (G0 %) without ntTiO₂/ATAB was also prepared and used in all tests. The adhesives were analyzed for degree of conversion (DC%), softening in solvent, radiopacity, antibacterial activity against saliva-derived microcosm, mineral deposition capability, and cytotoxicity.
RESULTS: Analytical techniques, including TEM, FTIR, UV-Vis, and micro-Raman spectroscopy, confirmed the structure and chemical composition of the ntTiO₂/ATAB. A DC% over 60 % was observed for all groups, with no adverse impact on radiopacity or softening in solvent. Antibacterial testing indicated that increasing ntTiO₂/ATAB concentration led to reduced colony-forming units of critical microorganisms, with this effect sustained over a one-year aging period. Mineral deposition tests showed enhanced phosphate presence over the samples with higher ntTiO₂/ATAB concentrations. There were no statistical differences in human cell viability among groups.
SIGNIFICANCE: The dental adhesives formulated with ntTiO2/ATAB demonstrated suitable physical and chemical properties, including reliable bond strength to dentin previously tested. They also exhibited antibacterial effects against caries-related microorganisms even after aging, promoted bioactivity through mineral deposition, and showed no cytotoxicity against human cells. These adhesives represent a promising strategy to assist in reducing the risk of recurrent caries and preserve the material-dentin interface properties over time.
METHODS: ntTiO₂/ATAB was synthesized, characterized, and added into an experimental adhesive resin. The filler ntTiO₂/ATAB was added at 1, 2.5, and 5 wt% (G1 %, G2.5 %, G5 %) in the adhesive. A control group (G0 %) without ntTiO₂/ATAB was also prepared and used in all tests. The adhesives were analyzed for degree of conversion (DC%), softening in solvent, radiopacity, antibacterial activity against saliva-derived microcosm, mineral deposition capability, and cytotoxicity.
RESULTS: Analytical techniques, including TEM, FTIR, UV-Vis, and micro-Raman spectroscopy, confirmed the structure and chemical composition of the ntTiO₂/ATAB. A DC% over 60 % was observed for all groups, with no adverse impact on radiopacity or softening in solvent. Antibacterial testing indicated that increasing ntTiO₂/ATAB concentration led to reduced colony-forming units of critical microorganisms, with this effect sustained over a one-year aging period. Mineral deposition tests showed enhanced phosphate presence over the samples with higher ntTiO₂/ATAB concentrations. There were no statistical differences in human cell viability among groups.
SIGNIFICANCE: The dental adhesives formulated with ntTiO2/ATAB demonstrated suitable physical and chemical properties, including reliable bond strength to dentin previously tested. They also exhibited antibacterial effects against caries-related microorganisms even after aging, promoted bioactivity through mineral deposition, and showed no cytotoxicity against human cells. These adhesives represent a promising strategy to assist in reducing the risk of recurrent caries and preserve the material-dentin interface properties over time.