Biofabrication of poly(l-lactide-co-ε-caprolactone)/silk fibroin scaffold for the application as superb anti-calcification tissue engineered prosthetic valve.

In this study, electrospun scaffolds were fabricated by blending poly(l-lactide-co-ε-caprolactone) (PLCL) and silk fibroin (SF) with different ratios, and further the feasibility of electrospun PLCL/SF scaffolds were evaluated for application of tissue engineered heart valve (TEHV). Scanning electron microscopy (SEM) results showed that the surface of PLCL/SF electrospun scaffolds was smooth and uniform while the mechanical properties were appropriate as valve prosthesis. In vitro cytocompatibility evaluation results demonstrated that all of the PLCL/SF electrospun scaffolds were cytocompatible and valvular interstitial cells (VICs) cultured on PLCL/SF scaffolds of 80/20 & 70/30 ratios exhibited the best cytocompatibility. The in vitro osteogenic differentiation of VICs including alkaline phosphatase (ALP) activity and quantitative polymerase chain reaction (qPCR) assays indicated that PLCL/SF scaffolds of 80/20 & 90/10 ratios behaved better anti-calcification ability. In the in vivo calcification evaluation model of rat subdermal implantation, PLCL/SF scaffolds of 80/20 & 90/10 ratios presented better anti-calcification ability, which was consistent with the in vitro results. Moreover, PLCL/SF scaffolds of 80/20 & 70/30 ratios showed significantly enhanced cell infiltration and M2 macrophage with higher CD206+/CD68+ ratio. Collectively, our data demonstrated that electrospun scaffolds with the PLCL/SF ratio of 80/20 hold great potential as TEHV materials.