Journal of prosthodontics : official journal of the American College of Prosthodontists · 2024
The impact of Streptococcus mutans biofilms on the color stability and topographical features of three lithium disilicate ceramics.
СтатьяНазвание и аннотация: Перевод пока не подготовлен
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Balhaddad Abdulrahman A, Al Otaibi Abdulkareem Muneer, Alotaibi Khalid Saud, Al-Zain Afnan O, Ismail Eman H, Al-Dulaijan Yousif A, Alalawi Haidar, Al-Thobity Ahmad M
Аннотация
PURPOSE: Secondary caries around ceramic restorations is the most common reason for the replacement of fixed dental prostheses (FDPs). Therefore, it is important to examine the susceptibility of different ceramic materials to biofilm formation. This study aimed to evaluate biofilm development and associated roughness and color alterations in three lithium disilicate ceramics: Emax CAD (EC), Emax Press (EP), and LiSi Press (LP).
MATERIALS AND METHODS: Streptococcus mutans biofilms were grown on the three ceramics (n = 10 per group) for 7 days. Surface roughness values and color alteration were assessed before and after the biofilm using a non-contact profilometer and spectrophotometer, respectively. Biofilm growth was evaluated using colony-forming units (CFUs) and scanning electron microscope (SEM) images. The data were analyzed using one-way ANOVA and Tukey tests.
RESULTS: There was a significant (p ≤ 0.001) growth of S. mutans colonies on EC (6.75 ± 0.56) and EP (6.72 ± 0.54) specimens compared to LP, which showed no biofilm growth. The change in average surface roughness (∆Ra, nm) was significantly lower (p < 0.001) in the EC specimens (0.029 ± 0.003) compared to the EP (0.055 ± 0.012) and LP (0.041 ± 0.010). When the changes in the Rv and Rt values were investigated, no significant difference was observed among the groups. Following the biofilm challenge, the change in color (∆E00) was significantly lower (p = 0.005) in the LP group (1.68 ± 1.45) compared to the EC group (3.89 ± 1.50) and no significant difference was observed between the EP group (2.74 ± 1.01) and the other two ceramics (p ≥ 0.05).
CONCLUSION: LP ceramics exhibited superior resistance to S. mutans biofilm formation and associated changes in surface roughness and color compared to the Emax CAD and Emax Press ceramics. These findings suggest that the LiSi Press material may be more favorable to mitigate the risk of secondary caries.
MATERIALS AND METHODS: Streptococcus mutans biofilms were grown on the three ceramics (n = 10 per group) for 7 days. Surface roughness values and color alteration were assessed before and after the biofilm using a non-contact profilometer and spectrophotometer, respectively. Biofilm growth was evaluated using colony-forming units (CFUs) and scanning electron microscope (SEM) images. The data were analyzed using one-way ANOVA and Tukey tests.
RESULTS: There was a significant (p ≤ 0.001) growth of S. mutans colonies on EC (6.75 ± 0.56) and EP (6.72 ± 0.54) specimens compared to LP, which showed no biofilm growth. The change in average surface roughness (∆Ra, nm) was significantly lower (p < 0.001) in the EC specimens (0.029 ± 0.003) compared to the EP (0.055 ± 0.012) and LP (0.041 ± 0.010). When the changes in the Rv and Rt values were investigated, no significant difference was observed among the groups. Following the biofilm challenge, the change in color (∆E00) was significantly lower (p = 0.005) in the LP group (1.68 ± 1.45) compared to the EC group (3.89 ± 1.50) and no significant difference was observed between the EP group (2.74 ± 1.01) and the other two ceramics (p ≥ 0.05).
CONCLUSION: LP ceramics exhibited superior resistance to S. mutans biofilm formation and associated changes in surface roughness and color compared to the Emax CAD and Emax Press ceramics. These findings suggest that the LiSi Press material may be more favorable to mitigate the risk of secondary caries.