Exploring performance and mechanism of modified metal-organic frameworks in calcium alginate/polyvinyl alcohol double-network hydrogels for effective dye wastewater treatment.

To address the growing problem of dye wastewater pollution, a novel MOFs adsorbent calcium alginate/polyvinyl alcohol@UiO-66 was developed using environmentally friendly polymers, sodium alginate and polyvinyl alcohol creating gel spheres with a double-network structure through cross-linking. UiO-66 metal-organic frameworks are then grown onto the gel spheres, resulting in the final CA/PVA@UiO-66 adsorbent. This adsorbent boasts a high surface area (17.4 m2/g) and a mesoporous-nested microporous structure. It effectively removes MB from water, the actual maximum adsorption capacity was measured at 275.8 mg/g, which surpasses most existing adsorbents. Remarkably, the adsorbent retains 93.9 % of its initial capacity even after 10 reuse cycles. The adsorption process adhered to the Redlich-Peterson model and the PFO model. The N2-Sorption isotherm, actual Methylene blue (MB) adsorption experiments, and model analysis further suggest that the adsorption process is a complex heterogeneous diffusion process involving simultaneous chemical and physical adsorption. Additionally, the adsorption process is endothermic, indicating that it can occur spontaneously at 298 K. Increasing the temperature promotes the forward progress of the adsorption reaction, thereby enhancing the adsorption capacity. The gel adsorbent exhibited excellent dye wastewater purification capabilities, coupled with commendable reusability.